Studies on Wollastonite Ceramics as Low Loss Dielectrics
نویسندگان
چکیده
منابع مشابه
An investigation on Mechanical Properties of Apatite-Wollastonite-Diopside Glass-Ceramics Composites
Apatite-wollastonite (A-W)-phlogopite glass-ceramic is considered to be difficult to resorb, but often, it has been incorporated in particulate form to create new bioactive composites for potential maxillofacial applications. With various compositions, the present work has attempted to prepare apatite-wollastonite (A-W)-phlogopite glass ceramic composites, by applying sintering. Here, three-poi...
متن کاملLow-k interlevel dielectrics technology
Semiconductor manufacturers have been shrinking transistor size in integrated circuits (IC) to improve chip performance. This has resulted in increased speed and device density, both of which were described well by what is known as Moore’s Law – chip performance will double every ~18 months. The speed of an electrical signal in an IC is governed by two components – the switching time of an indi...
متن کاملThe In Vitro Bioactivity, Degradation, and Cytotoxicity of Polymer-Derived Wollastonite-Diopside Glass-Ceramics
Ca-Mg silicates are receiving a growing interest in the field of bioceramics. In a previous study, wollastonite-diopside (WD) glass-ceramics were successfully prepared by a new processing route, consisting of the heat treatment of a silicone resin embedding reactive oxide particles and a Ca/Mg-rich glass. The in vitro degradation, bioactivity, and cell response of these new WD glass-ceramics, f...
متن کاملLaser Machining and In Vitro Assessment of Wollastonite-Tricalcium Phosphate Eutectic Glasses and Glass-Ceramics
Bioactivity and ingrowth of ceramic implants is commonly enhanced by a suitable interconnected porous network. In this work, the laser machining of CaSiO₃‒Ca₃(PO₄)₂ biocompatible eutectic glass-ceramics and glasses was studied. For this purpose, 300 µm diameter craters were machined by using pulsed laser radiation at 532 nm with a pulsewidth in the nanosecond range. Machined samples were soaked...
متن کاملInduced crystallization porosity and properties of sintereds diopside and wollastonite glass-ceramics
diopside (CaO·MgO·2SiO2) and wollastonite (CaO·SiO2) glass-ceramics, forming ∼60% crystal phase and ∼40% albite-like Na2O·Al2O3·6SiO2) residual glass were studied. Two other diopside glass-ceramics with higher Na2O and Al2O3 content were also investigated. The phase formation was estimated by DTA, XRD and pycnometry, while the densification process was evaluated by porosity variations, ilatomet...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Association, Japan
سال: 1979
ISSN: 0009-0255,1884-2127
DOI: 10.2109/jcersj1950.87.1009_460