Casting Process Design and Wear Properties of a High Chromium Cast Iron Hammer
Article history: Received: 13.04.2015. Received in revised form: 13.07.2015. Accepted: 15.07.2015. In this article, both chemical composition and structure of a high chromium iron hammer head were designed and analyzed respectively. Also, the casting process was investigated and optimized through numerical simulation using commercial software View Cast. On the basis of numerical simulation and ...
متن کاملDelamination Wear Mechanism in Gray Cast Irons
An investigation of the friction and sliding wear of gray cast iron against chromium plated cast irons was carried out on a newly constructed reciprocating friction and wear tester. The tests were the first to be done on the test rig under dry conditions and at the speed of 170 cm/min, and variable loads of 20-260 N for a duration of 15 min. to 3 hours. The gray cast iron surfaces worn by a pro...
متن کاملCast Iron Metallurgy
Cast iron (CI) is one of the oldest materials in commercial use. It has excellent compressive strength and is commonly used for structures that require this property, as well as for water and sewer lines. This article explains CI metallurgy and why the understanding of this metallurgy is key to understanding other ferrous materials and alloys. The composition of cast iron (CI) varies significan...
متن کاملCast iron component failure: A metallurgical investigation
A fractured nutcracker was examined for determining the root cause/s for premature fracture/failure. This is one of the common tools used typically for cracking hard nuts. In this study, metallurgical failure analysis techniques namely, visual inspection, optical microscopy, SEM, and hardness tests were used in investigating the broken product. From the metallurgical analysis, it was determined...
متن کاملCutting Forces and Tool Wear Investigation for Face Milling of Bimetallic Composite Parts Made of Aluminum and Cast Iron Alloys
Bimetallic parts are used in many industries for weight and cost reduction of workpieces working under high loads and wear. One application for this type of composite material is in automotive industry. In this work the tool wear and cutting forces in the face milling of bimetallic parts made of aluminum and cast iron were investigated. A356 and GG25 alloys that are common materials for bimetal...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of Materials Science
سال: 1980
ISSN: 0250-4707,0973-7669
DOI: 10.1007/bf02748533