Structure–Phase Transitions in the Friction Contact Zone of High-Nitrogen Chromium–Manganese Austenitic Steel
نویسندگان
چکیده
The influence of contact stresses on the phase and concentration composition thin surface layers wear products in tribological zone high-nitrogen FeMn22Cr18N0.83 steel was studied using Mössbauer spectroscopy, X-ray structural analysis, electron microscopy. It shown that compressive developing under conditions dry sliding friction (20–25 microns) resulted strain-induced dissolution cellular precipitation (nitrides Cr2N) increased average content nitrogen austenite. Antiferromagnetic ordering austenite caused by secondary nitrides with low chromium observed tiny external (~0.1 adhesive wear. effect tension formation martensite α″-Fe16N2 structures established products.
منابع مشابه
Microstructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملInfluence of rotational speed on the development of microstructure in a friction stir welded 304 austenitic stainless steel
Friction stir welding was conducted on AISI 304 austenitic stainless steel sheet with dimensions of 100 mm × 100 mm × 2 mm. The FSW was performed at a welding speed of 150 mm/min and rotational speeds of 400 and 800 rpm. The results showed that high frequency of low angle grain boundaries (LAGBs) were formed through dynamic recovery in the thermo-mechanically affected zone (TMAZ). Higher amoun...
متن کاملfocus on communication in iranian high school language classes: a study of the role of teaching materials in changing the focus onto communication in language classes
چکیده ارتباط در کلاس به عوامل زیادی از جمله معلمان، دانش آموزان، برنامه های درسی و از همه مهم تر، مواد آموزشی وابسته است. در تدریس ارتباطی زبان که تاکید زیادی بر توانش ارتباطی دارد، کتاب درسی به عنوان عامل موثر بر پویایی کلاس محسوب میگردد که درس ها را از طریق فراهم آوردن متن ارتباط کلاسی و هم چنین نوع تمرین زبانی که دانش آموزان در طول فعالیت های کلاسی به آن مشغول اند، کنترل می کند. این حقیقت ک...
15 صفحه اولMicrostructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملAn investigation on the passivation behavior of nitrogen enriched AISI 316L austenitic stainless steel
In the present work the effects of plasma nitridization on the passivation behavior of AISI 316L was investigated. To do this; nitriding treatments were carried out at 420°C for 1, 2, 4 and 16 hours. The phase composition and structure of the nitrided layer were studied by Low Angle X-ray diffraction and Scanning Electron Microscopy. The hardness of samples also was evaluated by Vickers microha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2023
ISSN: ['2075-4701']
DOI: https://doi.org/10.3390/met13081433