Ultra-Fine Grained Dual-Phase Steels
This paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. A laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...
متن کاملultra-fine grained dual-phase steels
this paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. a laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...
متن کاملProperties of Fine–Grained Steels Generated by Displacive Transformation
It has been possible in recent times to make large quantities of steels in which the controlling scale is 20 nm or less, i.e., comparable to that of carbon nanotubes. The mechanical properties of such steels are abnormal. For example, in some cases the ductility vanishes as the strength increases, whereas in others the ductility almost entirely consists of uniform plastic strain. Some of the st...
متن کاملHigh Temperature Behavior of Dual Phase Steels
Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...
متن کاملA study on the sub-structure and mechanical properties of friction stir processed AA 6061-T6 joints with ultra-fine grained structure
Ultra-fine grained (UFG) structure (~0.6 µm) was produced in the stir zone (SZ) of 6061-T6 aluminum alloy joints using friction stir processing (FSP) cooled by liquid nitrogen (N2). A new experimental set-up was used to simultaneously quench the lower and upper surfaces of the samples during the processing. In addition, FSPed joints, using a steel backing plate, were produced at room temperatur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microscopy and Microanalysis
سال: 2018
ISSN: 1431-9276,1435-8115
DOI: 10.1017/s1431927618011649