Structure and thermo-mechanical response of Na2O-TiO2-SiO2 glasses to temperature
نویسندگان
چکیده
منابع مشابه
Interaction between Deformation and Crack Initiation under Vickers Indentation in Na2O–TiO2–SiO2 Glasses
An observed minimum in the critical crack initiation load at Poisson’s ratio (ν) of 0.21–0.22 in Na2O–TiO2–SiO2 glasses was investigated. Vickers indentation was used to examine hardness and average cracking length, fracture toughness was measured through the single-edge pre-cracked beam method, and volumes of densification and shear flow around indents were measured using atomic force microsco...
متن کاملMagnetic properties of praseodymium ions in Na2O–Pr2O3–SiO2 glasses
Sodium praseodymium silicate glasses of nominal composition 0.3Na2O xPr2O3 (0.7 x)SiO2, where 0pxp0:10; have been studied by magnetisation and X-ray photoelectron spectroscopy (XPS). The magnetisation data fail to collapse to a single curve in the M versus H=T representation for all values of x and the spread increases with x; indicating an increase in the magnetic exchange interaction. The M v...
متن کاملStructural Investigation of Na2O–B2O3–SiO2 Glasses Doped with NdF3
Abstract—Sodium borosilicate glasses doped with different content of NdF3 mol % have been prepared by rapid quenching method. Ultrasonic velocities (both longitudinal and shear) measurements have been carried out at room temperature and at ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature, softening temperature and Poisson's ratio have been obtained as a function of NdF3 modifier...
متن کاملX-ray photoelectron spectroscopy of CeO2–Na2O–SiO2 glasses
A series of (CeO2)x–(Na2O)0.3–(SiO2)(0.7−x) glasses, where 0.025≤ x≤ 0.075, have been synthesized and investigated by mean of X-ray photoelectron spectroscopy (XPS). The Ce 3d spin-orbit doublet was curve fitted in order to quantify the proportions of each cerium oxidation state in these glasses. It was found that Ce ions are predominantly in the Ce(III) state in glasses with compositions x≤ 0....
متن کاملViscosity and diffusion of barium and fluoride in Na2O/K2O/Al2O3/SiO2/BaF2 glasses
The interdiffusion coefficients of barium and fluoride in glasses, in the system Na2O/K2O/Al2O3/SiO2 with BaF2 additions, were determined from the diffusion profiles using energy dispersive X-ray analysis in a scanning electron microscope. The diffusivities were in agreement with Arrhenius-equation. Diffusion coefficients of fluoride were in the range from 4.5 10 15 m s 1 to 30 10 15 m s 1 at 5...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Non-Crystalline Solids
سال: 2016
ISSN: 0022-3093
DOI: 10.1016/j.jnoncrysol.2016.09.020