Structure and Properties of Regenerated Cellulose Fibers Spun from Organic Slvent
نویسندگان
چکیده
منابع مشابه
Properties of Lignocellulosic Composites Containing Regenerated Cellulose Fibers
The aim of the paper was to examine the application of regenerated cellulose fibers as a reinforcement material in particleboard production. Single-layer, 10 mm thick panels, with the density of 800 kg/m3 were produced with addition of regenerated cellulose fibers in the range of 0 do 15% by mass during panels’ production. The mechanical and physical parameters of the produced panels were teste...
متن کاملTransitional Properties of Cotton Fibers from Cellulose I to Cellulose II Structure
Mercerized fibers were prepared from native cotton fabrics via NaOH solution treatment at different concentrations. Mercerization led to transformation of the crystal structure of cotton fibers from cellulose I to II when the NaOH concentration was greater than 10 wt%. In addition, the cotton fibers were converted into a swollen and rough state after mercerization treatment. The results of Four...
متن کاملDeformation mechanisms in ionic liquid spun cellulose fibers
The molecular deformation and crystal orientation of a range of next generation regenerated cellulose fibers, produced from an ionic liquid solvent spinning system, are correlated with macroscopic fiber properties. Fibers are drawn at the spinning stage to increase both molecular and crystal orientation in order to achieve a high tensile strength and Young’s modulus for potential use in enginee...
متن کاملextraction and acetylation of purified trypsin from bovin pancreas and study of some its physico-chemical properties
آنزیم تریپسین در شرایط قلیایی ناپایدار می باشد .و فعالیت پروتئولیتیکی تریپسین منجربه خود هضمی آن در جایگاههای خاصی می گردد. بنابر این آنزیمی با ناپایداری بالا محسوب میگردد. در سالهای اخیر موفق شدند که با ایجاد تغیرات شیمیایی با اضافه کردن فلزات خاص ، کلسیم و یا عمل استیلاسیون منجر به افزایش پایداری آنزیم تریپسین گردند. مطالعات در حال حاضر نشان می دهد که تریپسین استیله شده فعالیت آنزیمی خود را ...
15 صفحه اولDry-Spun Neat Cellulose Nanofibril Filaments: Influence of Drying Temperature and Nanofibril Structure on Filament Properties
Cellulose nanofibrils (CNF) were spun into filaments directly from suspension without the aid of solvents. The influence of starting material properties and drying temperature on the properties of filaments produced from three different CNF suspensions was studied. Refiner-produced CNF was ground using a microgrinder at grinding times of 50 and 100 minutes. Filament spinning was performed using...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Sen'i Gakkaishi
سال: 1997
ISSN: 0037-9875,1884-2259
DOI: 10.2115/fiber.53.p41