Structure Analysis of Zn-Al-Mg Coating on Steel Wire
نویسندگان
چکیده
منابع مشابه
Studies on defects in galvanized coating on steel wire
Causes for deposition of defective galvanized coating (lumpy deposition of coating during hot dip galvanizing) of carbon-steel wire have been investigated. It is established that the lumpy deposition is caused due to segregation of silicon on the surface of steel wire. Due to this change in composition of the steel at surface, the regions get modified and lie in Sandelin hyper reactive zone. Th...
متن کاملStudy on Mg/Al Weld Seam Based on Zn–Mg–Al Ternary Alloy
Based on the idea of alloying welding seams, a series of Zn-xAl filler metals was calculated and designed for joining Mg/Al dissimilar metals by gas tungsten arc (GTA) welding. An infrared thermography system was used to measure the temperature of the welding pool during the welding process to investigate the solidification process. It was found that the mechanical properties of the welded join...
متن کاملElectrodeposition of Nano Hydroxyapatite Coating on Biodegradable Mg-Zn Scaffold (TECHNICAL NOTE)
Magnesium has been recently recognized as a biodegradation metal for bone substitute application. In the present work, porous magnesium-zinc scaffolds were prepared by powder metallurgical process and nano hydroxyapatite (HAP) coating on the Mg-3Zn (wt.%) scaffold was prepared by pulse electrodeposition and alkali treatment processes to improve the corrosion resistance of scaffold. The results ...
متن کاملComprehensive Characterisation of a Newly Developed Mg–Dy–Al–Zn–Zr Alloy Structure
This is a report on the structure phases and precipitates in a newly developed Mg–10Dy–3Al–1Zn–0.2Zr alloy. Specimens from the cast alloy were heat treated at temperatures of 480 ◦C, 520 ◦C and 560 ◦C, all for 8 and 16 h, and subsequently quenched. The structures were then analysed using scanning and transmission electron microscopy, while the mechanical properties were investigated using micro...
متن کاملSTRUCTURE OF STABLE INTERMETALLIC COMPOUNDS OF THE Al-Li-Cu-(Mg) AND Al-Li-Zn-(Cu) SYSTEMS
The results of a thorough structural study of crystalline intermetallic compounds within the Al-Li-(Cu,Mg,Zn) system are given. Characteristic morphologies of these ternary or quaternary phases are exhibited by concentrated alloys or large single crystals. Typical X-ray powder diffraction data, selected area electron diffraction patterns and high resolution electron microscopy images are shown,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Research Papers Faculty of Materials Science and Technology Slovak University of Technology
سال: 2013
ISSN: 1338-0532,1336-1589
DOI: 10.2478/rput-2013-0012