Structural Rearrangement of 2-D Zeolite Nanosheets under Electron Beam
نویسندگان
چکیده
منابع مشابه
Morphological and structural evolution of WS2 nanosheets irradiated with an electron beam.
The morphological and structural evolution of WS2 nanosheets under electron irradiation is investigated using high-resolution transmission electron microscopy. During irradiation, the sulfur atoms that interacted with the electrons were sputtered first and the tungsten atoms began to sputter when the surrounding sulfur atoms had been sputtered. With an increasing irradiation time, the remaining...
متن کاملCrystallographic Structure Determination of MFI-Zeolite Nanosheets
Ultrathin MFI-zeolite nanosheets can be packed on porous supports to create molecular sieve membranes. The nanosheets on porous support reduce morphological damage seen in regular MFIzeolite crystals [1]. MFI-zeolite belongs to pentasil family of zeolites where the periodic building unit (PerBU) is composed of 12 interconnected SiO4 tetrahedral (T12) units of 41m2 (D2d) symmetry [2]. Rotation o...
متن کاملChemical and Structural Stability of Lithium-Ion Battery Electrode Materials under Electron Beam
The investigation of chemical and structural dynamics in battery materials is essential to elucidation of structure-property relationships for rational design of advanced battery materials. Spatially resolved techniques, such as scanning/transmission electron microscopy (S/TEM), are widely applied to address this challenge. However, battery materials are susceptible to electron beam damage, com...
متن کاملGrowth of zeolite crystals with graphene oxide nanosheets.
Growth of silicalite with graphene oxide (GO) nanosheets occurred via attachment of GO onto the silicalite surface, and entrapment of GO nanosheets inside single crystals. Electrically conductive composites were produced by calcination in nitrogen whereas silicalite crystals with slit-like mesopores of sizes 20-25 Å were obtained after GO burn-off.
متن کامل2D Zeolite Coatings: Langmuir-Schaefer Deposition of 3 nm Thick MFI Zeolite Nanosheets.
Stable suspensions of zeolite nanosheets (3 nm thick MFI layers) were prepared in ethanol following acid treatment, which partially removed the associated organic structure-directing agent. Nanosheets from these suspensions could then be dispersed at the air-water interface and transferred to silicon wafers using Langmuir-Schaefer deposition. Using layer-by-layer deposition, control on coating ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microscopy and Microanalysis
سال: 2015
ISSN: 1431-9276,1435-8115
DOI: 10.1017/s1431927615007400