Structural and Thermal Properties of a Selected Host Crystal Lattice: Exploration of Inherent Possibilities

Host Ba2MgSi2O7 phosphor was successfully prepared via low temperature combustion synthesis route. The phase identification of the done with help powder XRD technique. pattern revealed its monoclinic crystal symmetry a space group C2/c. have well clarified JCPDS PDF card no. #23-0842. average crystallite size calculated as 42nm and lattice strain 0.24, respectively. It is acquired that sample UV exposed for 15min gives optimum TL intensity at 112.190C displays single glow peak. On basis curve, it can be suggested (BMS) an efficient host but not better phosphor. In our present study, we discussed on XRD, FESEM thermo-luminescence (TL) characteristics different kinetic parameters this