Structural And Supercapacitive Performance Of V2O5 Thin Films Prepared By DC Magnetron Sputtering
نویسندگان
چکیده
منابع مشابه
CrNx Films Prepared by DC Magnetron Sputtering and High-Power Pulsed Magnetron Sputtering: A Comparative Study
CrNx (0 ≤ x ≤ 0.91) films synthesized using highpower pulsed magnetron sputtering, also known as high-power impulse magnetron sputtering (HiPIMS), have been compared with those made by conventional direct-current (dc) magnetron sputtering (DCMS) operated at the same average power. The HiPIMS deposition rate relative to the DCMS rate was found to decrease linearly with increasing emission streng...
متن کاملDEPOSITION OF THIN TiO2 FILMS BY DC MAGNETRON SPUTTERING METHOD
Sputter deposition process is another old technique being used in modern semiconductor industries. Sputtering is a process that can deposit TiO2 material on wafer/glass substrates. In this process target is connected to negative high voltage. Further argon gas is introduced into the chamber and is ionized to a positive charge. The positively charged argon atoms are attracted and strike the nega...
متن کاملAlNXOY THIN FILMS DEPOSITED BY DC REACTIVE MAGNETRON SPUTTERING
AlNxOy thin films were produced by DC reactive magnetron sputtering, using an atmosphere of argon and a reactive gas mixture of nitrogen and oxygen, for a wide range of partial pressures of reactive gas. During the deposition, the discharge current was kept constant and the discharge parameters were monitored. The deposition rate, chemical composition, morphology, structure and electrical resis...
متن کاملSuperhard NbB2-x thin films deposited by dc magnetron sputtering
We have deposited weakly textured substoichiometric NbB2-x thin films by magnetron sputtering from a NbB2 target. The films exhibit superhardness (42 ± 4 GPa), previously only observed in overstoichiometric TiB2 thin films, and explained by a self-organized nanostructuring, where thin TiB2 columnar grains hinder nucleation and slip of dislocations and a B-rich tissue phase between the grains pr...
متن کاملGrowth, structural, and magnetic properties of iron nitride thin films deposited by dc magnetron sputtering
FeN thin films were deposited on glass substrates by dc magnetron sputtering at different Ar/N2 discharges. The composition, structure and the surface morphology of the films were characterized using X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and atomic force microscopy (AFM). Films deposited at different nitrogen pressures exhibited different structures with different nit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOSR Journal of Applied Chemistry
سال: 2017
ISSN: 2278-5736,2278-5736
DOI: 10.9790/5736-1005026469