Structural and optical properties of Al-Tb/SiO2multilayers fabricated by electron beam evaporation

Structural and optical properties of Al-Tb/SiO2 multilayers fabricated by electron beam evaporation

control of the optical properties of nanoparticles by laser fields

در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...

Age Hardening of Ultrafine Grained Al-Ti-Cr Alloys Fabricated by Continuous Electron Beam Evaporation

Supersaturated Al-Ti-Cr alloys were produced by a continuous electron beam evaporation technique. The as-deposited alloy sheets were fcc supersaturated solid solution with an average grain size of about 400 nm. Due to the fine grain size, the hardness of the alloy was as high as 270Hv. The sheet showed age hardening, and the peak hardness of 340Hv was obtained after aging at 623K for 900 s, in ...

The Structural and Mechanical Properties of Al-2.5%wt. B4C Met-al Matrix Nano-composite Fabricated by the Mechanical Alloying

In this study, aluminum (Al) matrix reinforced with micro-particles (30 µm) and nano-particles (50 nm) boron carbide (B4C) were used to prepare Al-2.5%wt., B4C nano-composite and micro-composite, respectively, using mechanical alloying method. The mixed powders were mechanically milled at 5, 10, 15 and 20 hrs. The XRD results indicated that the crystallite sizes of both the micro-composite and ...

Effect of Particle Size on the Structural and Mechanical Properties of Al–AlN Nanocomposites Fabricated by Mechanical Alloying

Nanostructured Al composites with 2.5 wt.% aluminum nitride (AlN) were fabricated by powder metallurgy using mechanically milled aluminum powder mixed in a planetary ball mill with different particle sizes of AlN (50 nm and 1 μm) as reinforcement. After 20 h milling, the powders were die-pressed uniaxially in a steel die and then sintered at 670 °C for 2 h. The morphologies and properties of th...