Structural and Magnetic Response in Bimetallic Core/Shell Magnetic Nanoparticles
نویسندگان
چکیده
منابع مشابه
Structural and Magnetic Response in Bimetallic Core/Shell Magnetic Nanoparticles
Bimagnetic monodisperse CoFe₂O₄/Fe₃O₄ core/shell nanoparticles have been prepared by solution evaporation route. To demonstrate preferential coating of iron oxide onto the surface of ferrite nanoparticles X-ray diffraction (XRD), High resolution transmission electron microscope (HR-TEM) and Raman spectroscopy have been performed. XRD analysis using Rietveld refinement technique confirms single ...
متن کاملRetraction: Khan et al. Structural and Magnetic Response in Bimetallic Core/Shell Magnetic Nanoparticles. Nanomaterials 2016, 6, 72
It has come to our attention that Figure 3 of the title paper [1] contains unacceptable levels of image manipulation and thus does not provide firm evidence of the particles reported [...].
متن کاملThermal synthesis of Hematite nanoparticles: Structural, magnetic and morphological characterizations
Hematite (α-Fe2O3) nanoparticle was synthesized using organometallic compound - ferrocene carboxaldehyde through solventless solid state thermal decomposition technique. The crystal structure, magnetic and morphological properties of the decomposed material were studied using powder X-ray diffraction (XRD), superconducting quantum interference device (SQUID) magnetometry, ...
متن کاملStructural, Magnetic and Photocatalytic Properties of BiFeO3 Nanoparticles
Single phase BiFeO3 (BFO) nanoparticles as a visible light photocatalyst were successfully synthesized by thermal decomposition of the glyoxylate precursor. The glyoxylate precursors were formed by the redox reaction between ethylene glycol and nitrate ions. The phase evolution, structure and optical properties of BFO nanoparticles were characterized by X-ray diffraction, electron microscopy an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanomaterials
سال: 2016
ISSN: 2079-4991
DOI: 10.3390/nano6040072