Solid-State Diffusion Bonding of Commercially pure Titanium and Precipitation Hardening Stainless steel
Solid-state direct diffusion bonding of commercially pure Titanium (Cp-Ti) and precipitation hardening stainless steel (PHSS) has been carried out in the temperature range of 800°C to 1000°C with an interval of 50°C for 3.6 ks under 3.5 Mpa uniaxial load in (4 to 6)×10 Pa vacuum. The effects of temperatures have been investigated with reference to bond strength. The examination revealed that th...
متن کاملAccumulative Roll Bonding of Aluminum/Stainless Steel Sheets
An Al/Stainless Steel/Al lamellar composite was produced by roll bonding of the starting sheets at 400 °C. Afterward, the roll bonded sheet was cut in half and the accumulative roll bonding (ARB) process at room temperature was applied seven times. As a result, the central steel layer fractured and distributed in the Al matrix among different layers introduced by the repetition of roll bonding ...
متن کاملComposite rebonding to stainless steel metal using different bonding agents.
The purpose of this study was to determine the in vitro bond strengths of composite rebonded to stainless steel crown metal (SS) using five different bonding agents after composite to SS bond failure had been produced. The adhesive systems were applied to the failed bonds following the manufacturers' instructions and, as a control, composite was bonded to SS without using a bonding agent. Each ...
متن کاملComposite Bonding to Stainless Steel Crowns Using a New Universal Bonding and Single-Bottle Systems
Aim. The aim of this study is to evaluate the shear bond strength of nanocomposite to stainless steel crowns using a new universal bonding system. Material and Methods. Eighty (80) stainless steel crowns (SSCs) were divided into four groups (20 each). Packable nanocomposite was bonded to the lingual surface of the crowns in the following methods: Group A without adhesive (control group), Group ...
متن کاملThe Interaction between Hydrogen and Surface Stress in Stainless Steel
This paper reveals the interaction between hydrogen and surface stress in austenitic stainless steel by X-ray diffraction stress measurement and thermal desorption analysis before and after being charged with hydrogen. The surface residual stress was varied by surface finishing using several disc polishing agents. The obtained results show that the residual stress near surface had a significant...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallic Materials
سال: 2012
ISSN: 0023-432X
DOI: 10.4149/km_2012_3_193