Stress Corrosion Cracking Behavior of Carbon Steel in Aqueous Dipa and in Dipa-Sulfolane-Water Solutions
نویسندگان
چکیده
منابع مشابه
Effect of Hydrogen on Corrosion and Stress Corrosion Cracking of AZ91 Alloy in Aqueous Solutions
The effect of hydrogen on the corrosion and stress corrosion cracking of the magnesium AZ91 alloy has been investigated in aqueous solutions. Hydrogen produced by corrosion in water diffuses into, and reacts with the Mg matrix to form hydride. Some of the hydrogen accumulates at hydride/Mg matrix (or secondary phase) interfaces as a consequence of slow hydride formation and the incompatibility ...
متن کاملStress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC) in a nitrite-containing chloride solution. Slow strain rate testing (SSRT) in 30 wt. % MgCl₂ solution established SCC susceptibility, as evidenced by post-SSRT fractography. Addition of nitrite to the chloride solution, which is reported to have inhibitive influence on corrosion of stainless ste...
متن کاملErosion Corrosion of Carbon Steel in Aqueous Slurries
Erosion corrosion of an usual carbon steel in a variety of aqueous slurries of 10% Al2O3 powder composed of 0.1M NaOH, concentrated cooling water (synthetic rather than natural), 3% NaCl, and 0.01M HCl was investigated from the electrochemical point of view. The total weight loss, Wt, was experimentally divided into the following three terms: the mechanical loss, Wm, the corrosion loss, Wc, and...
متن کاملAn Electrochemical Model for Prediction of Corrosion of Mild Steel in Aqueous Carbon Dioxide Solutions
0010-9312/96/000067/$5.00+$0.50/0 © 1996, NACE International Submitted for publication December 1994; in revised form, July 1995. * Institutt for Energiteknikk, P.O. Box 40, N-2007, Kjeller, Norway. Present address: Department of Mechanical Engineering, University of Queensland, Brisbane, Qld. 4072, Australia. ** University of Saskatchewan, Saskatoon, Canada. Present address: Institutt for Ener...
متن کاملAn Investigation on Corrosion and Stress Corrosion Cracking initiation of a Ferritic Stainless Steel in a Tertiary Amine Solution
The present study focused on stress corrosion cracking (SCC) and corrosion behavior of ferritic stainless steel (grade 430) in activated methyl diethanolamine (aMDEA) solution, which is classified as a tertiary amine. In this regard, cyclic polarization and U-bend tests were performed in CO2 loaded aMDEA with different concentrations at 25 and 70 °C to observe corrosion behavior and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Zairyo-to-Kankyo
سال: 1992
ISSN: 0917-0480,1881-9664
DOI: 10.3323/jcorr1991.41.550