Strengthening Mechanisms of P/M Extruded Titanium Materials with Additive Hydrogen
نویسندگان
چکیده
منابع مشابه
Machinability of Sinter-hardening PM materials with experimental machining enhancers
Although powder metallurgy is an economical method for production of near net shape components, machining operations are often required to deliver desired geometrical features, dimensional tolerances, and surface finish of PM parts. Machining enhancers are used to improve the machinability of PM components and to increase tool life. MnS is the most common machinability enhancer used for PM stee...
متن کاملStrengthening Mechanisms in the Aged 2024 and 7075 Aluminium Alloys
Aluminum 2024 and 7075 alloys which are widely used in aerospace and marine applications were chosen to investigate their strengthening mechanisms. Using differential thermal analysis (DIA), metallography and tension tests, the best solutionizing conditions were determined to be 500±5°C and 2 hours for 2024 and 480?±5°C and 1 hour for 7075 alloy. Aging was performed in the range of 100 to 200°C...
متن کاملEvaluation of apically extruded bacteria associated with different nickel-titanium systems.
INTRODUCTION The aim of this in vitro study was to evaluate the amount of apically extruded bacteria associated with several root canal preparation systems. METHODS Forty-four extracted human mandibular premolar root canals were contaminated with an Enterococcus faecalis suspension. After incubation at 37°C for 24 hours, the root canals were instrumented using the Twisted File (SybronEndo, Or...
متن کاملStrengthening steel bridges with new high modulus CFRP materials
This paper presents the details and relevant findings of an experimental program which was conducted in three phases to investigate the behavior of steel-concrete composite bridge girders strengthened with new high modulus carbon fiber reinforced polymer (HM CFRP) materials. In the first phase, the feasibility of various lIM CFRP strengthening systems was examined. The second phase investigated...
متن کاملHydrogen Interaction with Euvl-relevant Optical Materials
Mo/Si multilayer mirrors were exposed to deuterium ions with well-defined energies in order to gain insight into the effects of Extreme UV light driven plasma generation on reflective elements in commercial lithography equipment. Post-irradiation analysis by Rutherford Backscattering Spectrometry (RBS) showed erosion of both Mo and Si layers for the highest energy (50 eV/D) and exposure time (5...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2013
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.60.467