Strength degradation of glass epoxy composites under hygrothermal environment
نویسندگان
چکیده
منابع مشابه
Environmental Effects on Mechanical Properties of Glass/Epoxy and Fiber Metal Laminates, Part I: Hygrothermal Aging
In this article, the effect of hygrothermal aging on mechanical properties of fiber metal laminates (FMLs) and E-glass/epoxy (GE) composites is investigated. First, FML and GE specimens were built using wet lay-up technique under vacuum pressure. Hygrothermal aging simulation was then carried out on both specimen types in distilled water at a constant temperature of 90 °C for 5 weeks. The resul...
متن کاملHygrothermal aging effects on fatique of glass fiber/polydiclopentadiene composites
We investigated the effects of hygrothermal aging on the tension–tension fatigue behavior of unidirectional (UD) glass/polydicyclopentadiene (pDCPD) composites. Samples were immersed in deionized (DI) water and salt water, and glass/epoxy composites were used as a benchmark for comparison. Composites of pDCPD showed less water uptake and superior fatigue performance compared to similarly aged e...
متن کاملCreep Behavior of Basalt and Glass Fiber Reinforced Epoxy Composites
The creep behavior of basalt fiber reinforced epoxy (BFRE) and glass fiber reinforced epoxy (GFRE) composites was studied through tensile testing at high temperature. To study the effect of reinforcing epoxy, the micro glass powder (MGP) was added at various volume percentage into the epoxy resin in BFRE composites. The initial strain for all the specimens were evaluated and compared with each ...
متن کاملA Shear Strength Degradation Model for Anisotropic Conductive Adhesive Joints Under Hygrothermal Conditions
Hygrothermal environments can degrade anisotropic conductive adhesive (ACA) joints by weakening the shear strength of adhesive interface. In this paper, the shear strength degradation model of ACA joints under hygrothermal conditions was formulated through experimental testing and theoretical modeling. The shear strength degradation data were obtained from different hygrothermal aging tests and...
متن کاملFatigue and ultrasonic testing of epoxy-glass composites
Purpose: The purpose of this paper was to find relationship between the degree of strength degradation caused by fatigue and the changes of ultrasonic wave characteristics such as wave velocity and damping coefficient. Design/methodology/approach: Epoxy-glass composites were subjected to oscillatory bending loadings with constant deflection. During fatigue procedure the force needed to achieve ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Today: Proceedings
سال: 2021
ISSN: 2214-7853
DOI: 10.1016/j.matpr.2020.08.778