Strain evolution around corrosion pits under fatigue loading
نویسندگان
چکیده
منابع مشابه
Damage Evolution in Composite Bonded Joints under Fatigue Loading
The fatigue behaviour of single lap bonded joints under fatigue loading was already investigated and a suitable life prediction model was presented and validated [1-2]. The model is based on the actual damage evolution under fatigue load: a crack initiation followed by its propagation up to a critical length [2, 3]. In the present paper the evolution of fatigue damage in single lap joints is ex...
متن کاملFatigue Analysis for Structures under Stochastic Loading
Predicting the peak distribution of stochastic stress responses is critical for various fatigue analysis problems with stochastic uncertainties. In this paper, a method, based on the first-order reliability method (FORM), is proposed for estimating the peak distribution of stochastic response. The method linearizes the stochastic process at the associated most probable point. After linearizatio...
متن کاملBiodegradation of polyurethane under fatigue loading.
A method utilizing expansion of a diaphragm-type film specimen was developed to study in vitro biodegradation of poly(etherurethane urea) (PEUU) under conditions of dynamic loading (fatigue). A finite element model was used to describe the strain state, which ranged from uniaxial at the edges of the film to balanced biaxial tensile strain at the center. During testing, the film was exposed to a...
متن کاملCumulative Fatigue Damage Under stepwise Tension-Compression Loading
Rock structures are subjected to cyclic tension-compression loading due to a blasting, earthquake, traffic and injection-production in underground storage case. Therefore study the fatigue behavior of rock samples under this type of loading is required. In this study, the accumulated fatigue damage for a Green Onyx rock sample which consisted of only one mineral composition with two-step high-l...
متن کاملStrain gradient plasticity under non-proportional loading
A critical examination is made of two classes of strain gradient plasticity theories currently available for studying micrometre-scale plasticity. One class is characterized by certain stress quantities expressed in terms of increments of strains and their gradients, whereas the other class employs incremental relationships between all stress quantities and the increments of strains and their g...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Theoretical and Applied Fracture Mechanics
سال: 2018
ISSN: 0167-8442
DOI: 10.1016/j.tafmec.2018.02.015