Stability of Ba-ferrite magnetic recording media.
نویسندگان
چکیده
منابع مشابه
Crystallographic and Magnetic Characteristics of Ba Ferrite Sputtered Films for High Density Magnetic Recording Disks
Ba ferrite films with non-stoichiometric composition were deposited using Facing Targets Sputtering apparatus. The films with well c-axis orientation and remarkable perpendicular anisotropy were attained even at the substrate temperature below 600°C. Sufficiently large saturation magnetization 4 w o f 3.7 kGand small crystallite size below 20 nm were attained using the targets with Fe-excessive...
متن کاملHigh Anisotropy CoPtCrB Magnetic Recording Media
We describe the synthesis, magnetism and structure of CoPtCrB alloys with Pt concentrations from 10 43 %. The Cr concentration in the alloys was 15-17 % and the B concentration was 9-11 %. The magnetic anisotropy and coercivity increase with increasing Pt up to M 30%, plateau at M 35,000 Oe and w 6000 Oe, respectively, and then decrease. Transmission electron microscopy results show the media f...
متن کاملRecording performances in perpendicular magnetic patterned media
We report on the recording performances and signal-to-noise ratio analyses of perpendicular magnetic bit-patterned media. Two different types of magnetic samples are investigated. They differ by the way that they were patterned (nano-imprint versus e-beam lithography) as well as their magnetic properties (Co/Pt multilayers and CoCrPt alloy are the recording layers). By using a contact read/writ...
متن کاملMagnetic Layers for Perpendicular Recording Media
Hard disk drives (HDDs) are recently being incorporated into video recorders, car navigation devices, family game machines, etc., as devices (AV-HDDs) to store digital AV (audio-visual) information such as movies and television programs. Because the AV-HDD has the features of large capacity, high speed and low cost, it is suitable for long-time recording, high-speed random access and multi-chan...
متن کاملPorous Ba Ferrite Prepared from Wood Template
Ba ferrite materials with porous microstructures were prepared from a natural cedar wood template in order to investigate new electromagnetic shielding materials. The wood templates were infiltrated with barium nitrate and iron nitrate solutions (molar ratio = 1:12) and dried to form ferrite gel, then, they were sintered in air at a temperature between 800 °C and 1400 °C. The 1-dimensional poro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1986
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.10.81