Highly textured BiFeO3(001) films were formed on L10-FePt(001) bottom electrodes on glass substrates by sputtering at reduced temperature of 400°C. Good electric polarization 2Pr = 80 and 95 μC/cm2, comparable to that of the reported epitaxial films, and coercivity Ec = 415 and 435 kV/cm are achieved in the samples with 20-nm- and 30-nm-thick electrodes. The BiFeO3(001) films show different deg...
متن کاملSputter deposition of PZT piezoelectric films on thin glass substrates for adjustable x-ray optics.
Piezoelectric PbZr(0.52)Ti(0.48)O(3) (PZT) thin films deposited on thin glass substrates have been proposed for adjustable optics in future x-ray telescopes. The light weight of these x-ray optics enables large collecting areas, while the capability to correct mirror figure errors with the PZT thin film will allow much higher imaging resolution than possible with conventional lightweight optics...
متن کاملThe mechanism of sputter-induced epitaxy modification in YBCO (001) films grown on MgO (001) substrates
The sputter-induced epitaxy change of in-plane orientation occurring in YBa2Cu3O72x (001) thin films grown on MgO (001) substrates by pulsed organo-metallic beam epitaxy (POMBE) is investigated by a series of film growth and characterization experiments, including RBS and TEM. The factors influencing the orientation change are systematically studied. The experimental results suggest that the su...
متن کاملStrain-induced polarization rotation in epitaxial (001) BiFeO3 thin films.
Direct measurement of the remanent polarization of high quality (001)-oriented epitaxial BiFeO3 thin films shows a strong strain dependence, even larger than conventional (001)-oriented PbTiO3 films. Thermodynamic analysis reveals that a strain-induced polarization rotation mechanism is responsible for the large change in the out-of-plane polarization of (001) BiFeO3 with biaxial strain while t...
متن کاملFerroelectric domain structures of epitaxial „001... BiFeO3 thin films
Ferroelectric domain structures of epitaxial BiFeO3 thin films on miscut 001 SrTiO3 substrates have been studied by transmission electron microscopy. BiFeO3 on 0.8° miscut substrates are composed of both 109° and 71° domains; in contrast, only 71° stripe domains are observed in BiFeO3 on 4° miscut 001 SrTiO3 substrates. The domain width in BiFeO3 on 4° miscut substrates increases as film thickn...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2012
ISSN: 1556-276X
DOI: 10.1186/1556-276x-7-435