Sprayed aluminium coating for corrosion protection under thermal gradient condition.
نویسندگان
چکیده
منابع مشابه
Alumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملCorrosion Protection of Metallic Waste Packages Using Thermal Sprayed Ceramic Coatings
Ceramic coated carbon steel coupons were corrosion tested in water with dissolved salts to simulate exposure to evaporation concentrated groundwater in an underground nuclear repository. Metallography revealed no corrosion at the ceramic metal interface of dense coatings, even though electrical measurements demonstrated that the coatings were slightly porous. Experimental results and a model to...
متن کاملThermal Sprayed Coatings Used Against Corrosion and Corrosive Wear
Coatings have historically been developed to provide protection against corrosion and erosion that is to protect the material from chemical and physical interaction with its environment. Corrosion and wear problems are still of great relevance in a wide range of industrial applications and products as they result in the degradation and eventual failure of components and systems both in the proc...
متن کاملHigh-temperature degradation of plasma sprayed thermal barrier coating systems
Thermal barrier coating systems (TBCs) are used in gas turbines to prevent high-temperature degradation of metallic materials in the combustor and turbine. One of the main concerns regarding TBCs is poor reliability, and accurate life prediction models are necessary in order to fully utilise the beneficial effects of TBCs. This research project aims at developing deeper understanding of the deg...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 1985
ISSN: 0288-4771
DOI: 10.2207/qjjws.3.712