Spinodal decomposition in Fe-Mo-Co and Fe-Mo-V ternary systems.

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Interdiffusion of Refractory Elements in Fe-Cr-X (X-Mo, W) and Fe-Mo-W Ternary Iron Alloys

Interdiffusion coefficients of the refractory elements in Fe-Cr-X (X 1⁄4 Mo, W) and Fe-Mo-W ternary alloys were measured on the basis of the modified Boltzmann-Matano method for ternary systems. The cross interdiffusion coefficient, ~ D CrW was positive in Fe-Cr-W ternary alloy, indicating that W accelerates interdiffusion between Fe and Cr atoms. On the other hand, the cross interdiffusion coe...

متن کامل

Composition, Morphology, and Topography of Galvanic Coatings Fe-Co-W and Fe-Co-Mo

Ternary coatings Fe-Co-W with an iron content of 40-55 at.%, cobalt 39-44 at.%, and tungsten 4-12 at.% and Fe-Co-Mo with an iron content of 40-55 at.%, cobalt 39-44 at.%, and tungsten 4-12 at.% were obtained by galvanostatic and pulse electrolysis on the mild steel substrate from iron(III) citrate-based electrolyte. The influence of electrolysis mode and parameters on composition of deposited a...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Transactions of the Iron and Steel Institute of Japan

سال: 1985

ISSN: 0021-1583,1881-1183

DOI: 10.2355/isijinternational1966.25.159