Spin-Controlled Photoluminescence in Hybrid Nanoparticles Purple Membrane System.
Spin-dependent photoluminescence (PL) quenching of CdSe nanoparticles (NPs) has been explored in the hybrid system of CdSe NP purple membrane, wild-type bacteriorhodopsin (bR) thin film on a ferromagnetic (Ni-alloy) substrate. A significant change in the PL intensity from the CdSe NPs has been observed when spin-specific charge transfer occurs between the retinal and the magnetic substrate. Thi...
متن کاملSpin-dependent electron transmission through bacteriorhodopsin embedded in purple membrane.
Spin-dependent photoelectron transmission and spin-dependent electrochemical studies were conducted on purple membrane containing bacteriorhodopsin (bR) deposited on gold, aluminum/aluminum-oxide, and nickel substrates. The result indicates spin selectivity in electron transmission through the membrane. Although the chiral bR occupies only about 10% of the volume of the membrane, the spin polar...
متن کاملMechanisms of Visible Photoluminescence from Size-Controlled Silicon Nanoparticles
We have observed visible photoluminescence (PL) spectra (peak energy: 3.1 eV) of size-controlled silicon (Si) nanoparticles annealed in oxygen gas. The PL peak energy did not depend on the temperature, and the PL lifetime was relatively fast (on the order of nanoseconds). It was inferred that the visible PL was attributed to localized states in the oxidized surfaces of size-controlled Si nanopa...
متن کاملPhotoluminescence of SnO2 nanoparticles embedded in Al2O3
Tetragonal Sn nanoparticles of ∼15 nm diameter are produced in Al2O3 by direct Sn implantation at room temperature. After thermal annealing at 1000 ◦C in oxygen, the implantation-induced amorphous region recrystallized and the Sn nanoparticles turned into SnO2 nanoparticles with an average diameter of ∼30 nm as revealed by transmission electron microscopy. While no absorption and photoluminesce...
متن کاملEmergence of Multicolor Photoluminescence in La0.67Sr0.33MnO3 Nanoparticles
Herein, we report the emergence of multicolor photoluminescence in a mixed-valence manganite nanoparticle La0.67Sr0.33MnO3 (LSMO NP) achieved through electronic structural modification of the nanoparticles upon functionalization with a biocompatible organic ligand, sodium tartrate. From UV−vis absorption, X-ray photoelectron spectroscopy (XPS), time-resolved photoluminescence study, and Raman s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ACS Nano
سال: 2016
ISSN: 1936-0851,1936-086X
DOI: 10.1021/acsnano.6b00333