Specimen size effect on superplastic flow behavior of electrodeposited nanocrystalline nickel
نویسندگان
چکیده
منابع مشابه
Deformation of electrodeposited nanocrystalline nickel
The mechanisms of deformation and damage evolution in electrodeposited, fully dense, nanocrystalline Ni with an average grain size of ~30 nm and a narrow grain size distribution were investigated by recourse to (i) tensile tests performed in situ in the transmission electron microscope and (ii) microscopic observations made at high resolution following ex situ deformation induced by compression...
متن کاملSample-size effects in the yield behavior of nanocrystalline nickel
The compressive plastic strength of nanometer-scale single-crystal metallic pillars is larger than that found in conventionally sized samples. This behavior is generally associated with a change in the length scale that determines plastic behavior and the consequent inability of nanoscale samples to store dislocations. Here, we show in the case of nanocrystalline nickel pillars, for which there...
متن کاملThe effect of saccharin on microstructure and corrosion behavior of nanocrystalline nickel thin films in alkaline solution
In this study the effect of crystallite size reduction and microstructure on the electrochemical corrosion behavior of nanocrystalline nickel (NC Ni) were investigated using Tafel polarization and electrochemical impedance spectroscopy (EIS) measurements in 10 wt.% NaOH. NC Ni coatings were produced by direct current electrodeposition using chloride baths in presence and absence of saccharin as...
متن کاملWear behavior of carbon steel electrodeposited by nanocrystalline Ni–W coating
Ni-W coatings, compared to pure nanocrystalline Ni, exhibit higher hardness and wear resistance. In some cases, these coatings are considered as environmental friendly alternatives for hard chromium coating. Till now, most of Ni-W coatings have been produced by direct current electrodeposition from alkaline baths. In this study square pulse current was used for deposition of Ni-W precipitates f...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Letters on Materials
سال: 2015
ISSN: 2218-5046,2410-3535
DOI: 10.22226/2410-3535-2015-3-264-268