Spasmodic growth during the rapid solidification of undercooled Ag-Cu eutectic melts
نویسندگان
چکیده
منابع مشابه
Effect of Sb Addition on the Solidification of Deeply Undercooled Ag-28.1 wt. % Cu Eutectic Alloy
Ag-28.1 wt. % Cu eutectic alloy solidifies in the form of eutectic dendrite at undercooling above 76 K. The remelting and ripening of the original lamellar eutectics result in the formation of the anomalous eutectics in the final microstructure. The addition of the third element Sb (0.5 and 1 wt. %) does not change the growth mode, but enlarges the volume fraction of anomalous eutectics because...
متن کاملNon-Equilibrium Solidification of Undercooled Metallic Melts
If a liquid is undercooled below its equilibrium melting temperature an excess Gibbs free energy is created. This gives access to solidification of metastable solids under non-equilibrium conditions. In the present work, techniques of containerless processing are applied. Electromagnetic and electrostatic levitation enable to freely suspend a liquid drop of a few millimeters in diameter. Hetero...
متن کاملDendrite Growth Kinetics in Undercooled Melts of Intermetallic Compounds
Solidification needs an undercooling to drive the solidification front. If large undercoolings are achieved, metastable solid materials are solidified from the undercooled melt. Containerless processing provides the conditions to achieve large undercoolings since heterogeneous nucleation on container walls is completely avoided. In the present contribution both electromagnetic and electrostatic...
متن کاملFormation of Cellular Structure on Metastable Solidification of Undercooled Eutectic CoSi-62 at. %
The relationship between emissivity, delay time, and surface growth for metastable solidification of CoSi-62 at. % eutectic alloys is reported from undercooling experiments conducted using electrostatic levitation. A fraction of the undercooled melt is first solidified to CoSi2 with subsequent nucleation in the mushy-zone of CoSi after an observed delay time. During this double recalescence eve...
متن کاملShort-range Order in Undercooled Melts and Its Impact on the Solidification Behaviour
As suggested by Frank [1] an icosahedral short-range order should be energetically favoured in undercooled metallic melts. Such a short-range order is predicted to influence the energy of the interface between the liquid and a solid nucleus, depending on the structure of the solid phase [2]. This in turn decisively impacts the nucleation behaviour of solid phases from the undercooled melt, and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Physics Letters
سال: 2013
ISSN: 0003-6951,1077-3118
DOI: 10.1063/1.4775670