Spark Plasma Sintering of Soft Magnetic Fe-Si-B-P-Cu Nanocrystalline Alloy in the Form of Magnetic Cores
نویسندگان
چکیده
منابع مشابه
Production of Nanocrystalline (Fe, Co)-Si-B-P-Cu Alloy with Excellent Soft Magnetic Properties for Commercial Applications
With the aim of applying to a magnetic core material, the effect of ribbon thickness on the magnetic properties of a (Fe, Co)-Si-B-P-Cu alloy ribbon was investigated. It is found that the Si addition in (Fe, Co)-Si-B-P-Cu nanocrystalline alloy increased the saturation magnetic flux density (Bs), but degraded the coercivity (Hc), suggesting that the Si addition should be suppressed to a little a...
متن کاملEffect of Cu Addition on Soft Magnetic Properties of Fe–Zr–Si Amorphous Alloy
The effect of Cu addition on the soft magnetic properties of FeZrSi amorphous alloy was investigated by X-ray analysis, TEM observation, and B-H curve tracer. As a melt-spun amorphous ribbon sample was annealed above the crystallization onset temperature, very fine ¡-Fe particles smaller than 315 nm were precipitated and uniformly distributed in an amorphous matrix. Cu addition to FeZrSi am...
متن کاملFabrication of Soft Magnetic Fe-based Nanoalloy
The Fe-Ni-Sb-B amorphous alloy has been prepared by a solid-solid chemical reaction of ferric trichloride, nickel chloride, antimony chloride and potassium borohydride powders at room temperature. The inductive couple plasma study indicates that the resultant is composed of Fe 5.38 %, Ni 56.19 %, Sb 29.02 % and B 0.44 %. The XRD and thermal analysis show that the alloy is a non-strict sense amo...
متن کاملEffect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کاملNanocrystalline Al7075 + 1 wt % Zr Alloy Prepared Using Mechanical Milling and Spark Plasma Sintering
The microstructure, phase composition, and microhardness of both gas-atomized and mechanically milled powders of the Al7075 + 1 wt % Zr alloy were investigated. The gas-atomized powder exhibited a cellular microstructure (grain size of a few µm) with layers of intermetallic phases along the cell boundaries. Mechanical milling (400 revolutions per minute (RPM)/8 h) resulted in a grain size reduc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2011
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.m2011233