Sorptivity and acid resistance of ambient-cured geopolymer mortars containing nano-silica
نویسندگان
چکیده
منابع مشابه
Acid Resistance of Fly ash based Geopolymer mortars
Geopolymers are a new promising binder manufactured by activation of a solid aluminosilicate source material with a highly alkaline activating solution and aided by heat. Fly ash, considered to be a waste material is rich in silica and alumina and hence can be used as a source material for manufacture of Geopolymers. These binders have been reported to achieve high early strength and better dur...
متن کاملPreparation and evaluation of geopolymer composites containing alumina particles at ambient temperature and after heating
In this research, geopolymer composites were prepared using metakaolin along with silica fume and potassium hydroxide as alkaline activators and alumina particles. The effect of alumina particle size to achieve castable microstructure and their mechanical properties were investigated. Different Si:Al mole ratio (1.5, 2, 2.5 and 3) and K:Si mole ratio (0.20, 0.25, 0.33) were formulated and the s...
متن کاملPreparation and Characterization of New Geopolymer-Epoxy Resin Hybrid Mortars
The preparation and characterization of metakaolin-based geopolymer mortars containing an organic epoxy resin are presented here for the first time. The specimens have been prepared by means of an innovative in situ co-reticulation process, in mild conditions, of commercial epoxy based organic resins and geopolymeric slurry. In this way, geopolymer based hybrid mortars characterized by a differ...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Cement and Concrete Composites
سال: 2016
ISSN: 0958-9465
DOI: 10.1016/j.cemconcomp.2016.06.017