Solvothermal synthesis of CdO and CuO nanocrystals
نویسندگان
چکیده
منابع مشابه
Low-temperature synthesis of LiFePO4 nanocrystals by solvothermal route
LiFePO4 nanocrystals were synthesized at a very low temperature of 170°C using carbon nanoparticles by a solvothermal process in a polyol medium, namely diethylene glycol without any heat treatment as a post procedure. The powder X-ray diffraction pattern of the LiFePO4 was indexed well to a pure orthorhombic system of olivine structure (space group: Pnma) with no undesirable impurities. The Li...
متن کاملSolvothermal synthesis of zincblende and wurtzite CuInS2 nanocrystals and their photovoltaic application.
We report a simple solvothermal synthesis approach to the growth of CuInS(2) nanocrystals with zincblende- and wurtzite-phase structures. Zincblende nanocrystals with particle sizes of 10-20 nm were produced using oleylamine as the solvent. When ethylenediamine was used as the solvent, similarly sized wurtzite nanocrystals with some degree of particle aggregation were formed. Use of a mixture o...
متن کاملSurfactant-controlled composition and crystal structure of manganese(II) sulfide nanocrystals prepared by solvothermal synthesis
We investigated how the outcome of the solvothermal synthesis of manganese(II) sulfide (MnS) nanocrystals (NCs) is affected by the type and amount of long chain surfactant present in the reaction mixture. Prompted by a previous observation that a larger than stoichiometric amount of sulfur is required [Puglisi, A.; Mondini, S.; Cenedese, S.; Ferretti, A. M.; Santo, N.; Ponti A. Chem. Mater. 201...
متن کاملSolvothermal synthesis and characterization of anatase TiO2 nanocrystals with ultrahigh surface area.
Phase-pure, ultrafine nanocrystalline anatase with high specific surface area (up to 250 m(2) g(-1)) was obtained upon injection of a titanium alkoxide precursor into ethanol with designed volume of water under mild solvothermal conditions (<200 degrees C, 2 h). Primary particle sizes were tuned by adjusting various reaction parameters, with the smallest grain sizes occurring at low temperature...
متن کاملSolvothermal soft chemical synthesis and characterization of plate-like particles constructed from oriented BaTiO3 nanocrystals
Plate-like BaTiO3 particles with a size of about 200 nm in thickness and 3 μm in width were prepared by using a novel solvothermal soft chemical process in ethanol and water-ethanol mixed solvents. A layered titanate of H1.07Ti1.73O4 with a lepidocrocite-like structure and plate-like nanoparticle morphology was used as the precursor, and solvothermally treated in the Ba(OH)2 solution to prepare...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chemical Physics Letters
سال: 2004
ISSN: 0009-2614
DOI: 10.1016/j.cplett.2004.06.092