Solidification microstructure and residual stress correlations in direct energy deposited type 316L stainless steel
نویسندگان
چکیده
منابع مشابه
Fatigue behavior of Austenitic Type 316L Stainless Steel
The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...
متن کاملEvolution of Microstructure and Residual Stress under Various Vibration Modes in 304 Stainless Steel Welds
Simultaneous vibration welding of 304 stainless steel was carried out with an eccentric circulating vibrator and a magnetic telescopic vibrator at subresonant (362 Hz and 59.3 Hz) and resonant (376 Hz and 60.9 Hz) frequencies. The experimental results indicate that the temperature gradient can be increased, accelerating nucleation and causing grain refinement during this process. During simulta...
متن کاملEngineering the residual stress state and microstructure of stainless steel with mechanical surface treatments
Four mechanical surface treatments have been considered for the application to austenitic stainless steel structures. Shot peening (SP), laser shock peening (LSP), ultrasonic impact treatment (UIT) and water jet cavitation peening (WJCP), also known as cavitation shotless peening (CSP), have been applied to 8 mm thick Type 304 austenitic stainless steel coupons. This study considers the merits ...
متن کاملSCC of 2304 Duplex Stainless Steel—Microstructure, Residual Stress and Surface Grinding Effects
The influence of surface grinding and microstructure on chloride induced stress corrosion cracking (SCC) behavior of 2304 duplex stainless steel has been investigated. Grinding operations were performed both parallel and perpendicular to the rolling direction of the material. SCC tests were conducted in boiling magnesium chloride according to ASTM G36; specimens were exposed both without extern...
متن کاملEffect of Changing Strain Rate on Flow Stress during Hot Deformation of Type 316L Stainless Steel
In industrial rolling, changes in strain rate and temperature occur with strain during passes, and between one pass and the next. Plane strain compression testing has been used with ramped changes in strain rate during deformation, and with changes in strain rate between two deformations to study their effects on flow stress. No systematic deviations from a mechanical equation of state were fou...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials & Design
سال: 2021
ISSN: 0264-1275
DOI: 10.1016/j.matdes.2021.109782