Solid Polymer Electrolyte‐Coated Macroporous Titania Nanotube Photoelectrode for Gas‐Phase Water Splitting

Photo corrosion of titania nanotubes within water splitting reaction

Titania nanotubes (TNT) prepared by anodization of Ti foils were used for water splitting in a standalone cell. The concentration polarization between the anode side (1M NaOH) and cathode side (0.5 M H2SO4) ensured that the water splitting reaction could take place with no external bias and separate H2 and O2 evolution could be achieved. The destructi...

Photo corrosion of titania nanotubes within water splitting reaction

Titania nanotubes (TNT) prepared by anodization of Ti foils were used for water splitting in a standalone cell. The concentration polarization between the anode side (1M NaOH) and cathode side (0.5 M H2SO4) ensured that the water splitting reaction could take place with no external bias and separate H2 and O2 evolution could be achieved. The destructi...

photo corrosion of titania nanotubes within water splitting reaction

titania nanotubes (tnt) prepared by anodization of ti foils were used for water splitting in a standalone cell. the concentration polarization between the anode side (1m naoh) and cathode side (0.5 m h2so4) ensured that the water splitting reaction could take place with no external bias and separate h2 and o2 evolution could be achieved. the destruction of tnt structures under 365 nm uv irradia...

Water Splitting: One‐dimensional TiO2 Nanotube Photocatalysts for Solar Water Splitting (Adv. Sci. 1/2017)

Controllable reduced black titania with enhanced photoelectrochemical water splitting performance.

Black titania prepared by metal-reduction methods is systematically studied and found the best controllable Mg-reduction method. Colored titania products from white, light blue, dark blue, to black were obtained with a crystalline/amorphous core-shell structure. The black titania shows a five times higher H2 production rate in photoelectrochemical (PEC) water splitting.