Sol-Gel Thin Films Immobilized with Bromocresol Purple pH-Sensitive Indicator in Presence of Surfactants
نویسندگان
چکیده
منابع مشابه
Enantioselective, chirally templated sol-gel thin films.
Enantioselective surfactant-templated thin films were fabricated through the sol-gel (SG) process. The enantioselectivity is general in the sense that it discriminates between pairs of enantiomers not used for the imprinting process. The chiral cationic surfactant (-)-N-dodecyl-N-methylephedrinium bromide (1) was used as the surfactant template, and after its extraction chiral domains were crea...
متن کاملThe production of Ceramic Thin Films by Sol-Gel Method
The purpose of this work was to production of ceramic thin films by using of Sol-Gel process. For this purpose deposition of SiO2 on substrates of soda-lime glasses has been carried out. Coating treatments on prepared specimen were conducted in a Sol solution by means of dipping at various times. After drying and performing appropriate heat treatment on each sample, the thickness of coated laye...
متن کاملThe production of Ceramic Thin Films by Sol-Gel Method
The purpose of this work was to production of ceramic thin films by using of Sol-Gel process. For this purpose deposition of SiO2 on substrates of soda-lime glasses has been carried out. Coating treatments on prepared specimen were conducted in a Sol solution by means of dipping at various times. After drying and performing appropriate heat treatment on each sample, the thickness of coated laye...
متن کاملStudies on sol-gel dip-coated nanostructured ZnO thin films
Nanostructured ZnO thin films were prepared by sol-gel dip coating technique. Zinc acetate and ammonium hydroxide were used as precursors and ethanol was as solvent. Ammonium hydroxide (NH4OH) solution was added drop-wise under vigorous stirring to obtain the sol-gel of different pH (varying from 6.9 to 7.2). ZnO thin films were obtained by dipping the glass substrates for few seconds and then ...
متن کاملStress effects in sol-gel derived ferroelectric thin films
Residual stress development during processing of sol-gel derived ferroelectric thin films influences electromechanical properties and performance. The present work investigates the effects of stress on field-induced polarization switching in ferroelectric Pb~Zr0.52Ti0.48)O3 ~PZT! ~52/48! thin films. Film response is measured as a function of externally applied mechanical stress using a double-b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISRN Analytical Chemistry
سال: 2012
ISSN: 2090-732X
DOI: 10.5402/2012/604389