Soft magnetic properties of multilayered Fe-2-4at%Si films.
نویسندگان
چکیده
منابع مشابه
Fabrication of Soft Magnetic Fe-based Nanoalloy
The Fe-Ni-Sb-B amorphous alloy has been prepared by a solid-solid chemical reaction of ferric trichloride, nickel chloride, antimony chloride and potassium borohydride powders at room temperature. The inductive couple plasma study indicates that the resultant is composed of Fe 5.38 %, Ni 56.19 %, Sb 29.02 % and B 0.44 %. The XRD and thermal analysis show that the alloy is a non-strict sense amo...
متن کاملEffect of Cobalt Concentration on Structural and Magnetic Properties of Co-Fe Thin Films
Co-Fe films were electrodeposited on Cu substrate from electrolytes with different Co concentration levels. X-ray diffraction (XRD) was used to investigate the films crystal structures. The results indicate that if the Co concentration is less that the Fe concentration, the cubic structure appears in the films, while the hexagonal structure dominates when the C...
متن کاملSoft Magnetic Properties of High-Entropy Fe-Co-Ni-Cr-Al-Si Thin Films
Soft magnetic properties of Fe-Co-Ni-Al-Cr-Si thin films were studied. As-deposited Fe-Co-Ni-Al-Cr-Si nano-grained thin films showing no magnetic anisotropy were subjected to field-annealing at different temperatures to induce magnetic anisotropy. Optimized magnetic and electrical properties of Fe-Co-Ni-Al-Cr-Si films annealed at 200 ◦C are saturation magnetization 9.13 × 105 A/m, coercivity 79...
متن کاملMagnetic properties and structure of Fe/Pt thin films
The structural transfqmation from fcc to fct and relevant magnetic properties of initially multilayered Fe/Pt films were studied. When the asdeposited FePt films were annealed at the temperature of 300°C and up, the fct-phase was formed. Rather square hysteresis loops and large coercivities were measured from the annealed films. The films annealed at 300°C retain a layered structure.
متن کاملStudy of Sputtered Fe/tSi/Fe Trilayer Films: Magnetic and Electronic Properties
A series of trilayers of sputtered Fe/Si/Fe were grown to study the interface characteristics and magnetic coupling between ferromagnetic Fe layers (30 Å thick) for Si spacer thickness (tSi) ranging from 15 Å to 40 Å. Grazing incidence x-ray diffraction, AFM, resistivity and x-ray photoelectron spectroscopy (XPS) measurements show substantial intermixing between the layers during deposition whi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1989
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.13.351