High-Frequency Behavior and Damping of Fe–Co–N-Based High-Saturation Soft Magnetic Films
Magnetization dynamics measurements at subnanosecond time scale have been performed on Fe–Co–N high-saturation soft magnetic films with Permalloy nanolayer seeds and having a saturation magnetization of 1.9 MA/m (1900 emu/cm). The damping parameter varies from 0.011 to 0.018, depending on applied bias field. The peak frequencies of the imaginary permeability spectra and the zero-crossing freque...
متن کاملSoft Magnetic Properties of High-Entropy Fe-Co-Ni-Cr-Al-Si Thin Films
Soft magnetic properties of Fe-Co-Ni-Al-Cr-Si thin films were studied. As-deposited Fe-Co-Ni-Al-Cr-Si nano-grained thin films showing no magnetic anisotropy were subjected to field-annealing at different temperatures to induce magnetic anisotropy. Optimized magnetic and electrical properties of Fe-Co-Ni-Al-Cr-Si films annealed at 200 ◦C are saturation magnetization 9.13 × 105 A/m, coercivity 79...
متن کاملarchitecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولThe high frequency magnetic properties of self assembled Fe–Co–Si–N nanogranular thin films
The effect of a variation in Si and N concentration on the microstructure, crystal structure and high-frequency magnetic properties of Fe–Co–Si–N nanogranular thin films was investigated. The films, prepared by rf magnetron sputtering, consisted of nanosized grains of FeCo as well as a Si and N rich intergranular amorphous phase. The Si concentration had a significant effect on the crystal stru...
متن کاملPhysical Properties of Reactively Sputter-Deposited C-N Thin Films
This work aims to prepare and study amorphous carbon nitride (CNx) films. Films were deposited by reactive magnetron radiofrequency (RF) sputtering from graphite target in argon and nitrogen mixture discharge at room temperature. The ratio of the gas flow rate was varied from 0.1 to 1. Deposited films were found to be amorphous. Highest Nitrogen concentration achieved was 42 atomic percent whic...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1991
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.15.303