Alumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملSmart Local Backup Protection for Smart Substation
Received Apr 11, 2017 Revised Apr 28, 2017 Accepted Jun 17, 2017 This paper presents a novel smart local backup protection SLBP used for the support and backup of the protective relays in a smart substation. The proposed SLBP is based on the IEC61850 standards and the concept consists of the acquisition of Generic Object Oriented Substation Event GOOSE used for tripping and interlocks exchange ...
متن کاملCurrent Oscillations in Epoxy-coated Steel at Anodic Polarization
The current oscillatory behavior of epoxy-coated low carbon steel at anodic polarization was investigated in 3,5 % and 0,5 % solutions of NaCl. It was established, that the coated steel may show current oscillations at potentiostatic anodic polarization. The oscillations are of different type, period and amplitude and are more clearly expressed in 0,5 % solution. The presented results might be ...
متن کاملalumina nanostructured coating for corrosion protection of 316l stainless steel
nanostructured alumina thin films were coated on stainless steel by sol-gel dip coating method. in order to prevent crack formation, al2o3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. effects of calcination temperature and withdrawal speed on structural properties were analyzed using xrd and sem. topography and thickness of coatings were analyzed by ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Progress in Organic Coatings
سال: 2015
ISSN: 0300-9440
DOI: 10.1016/j.porgcoat.2014.10.002