Sliding wear characteristics of sintered ferrous products surface treated by boriding and carburizing.
نویسندگان
چکیده
منابع مشابه
Sintered Steel Composites Reinforced with Ceramic Nanoparticles: Fabrication, Characteristics and Wear Behavior
Steel composites reinforced with alumina nanoparticles were prepared by powder metallurgy process. Samples containing two different amounts of carbon (0.35 and 0.55 wt.%) and 0-5 wt.% Al2O3 nanoparticles were fabricated by mixing, compacting and sintering of diffusion bonded Distaloy AE powder. The density, hardness and wear tests were performed on the prepared samples. Fu...
متن کاملComparison of Carburizing and Boronizing Processes on Mechanical and Wear Properties of PM Parts
In this study carburizing and boronizing processes were applied to powder metallurgy steel specimens and the mechanical and tribological properties of the substrate and coatings were evaluated under various process conditions.
The specimens, made from industrial test pieces, were carburized in a powder pack for a duration of 2-5 hrs at 850-950 ˚C. Similar specimens were pack boronized for 4 ...
متن کاملComparison of Carburizing and Boronizing Processes on Mechanical and Wear Properties of PM Parts
In this study carburizing and boronizing processes were applied to powder metallurgy steel specimens and the mechanical and tribological properties of the substrate and coatings were evaluated under various process conditions. The specimens, made from industrial test pieces, were carburized in a powder pack for a duration of 2-5 hrs at 850-950 ˚C. Similar specimens were pack boronized for 4 hr...
متن کاملSintered hydroxyapatite ceramic for wear studies.
A sintered hydroxyapatite (HAP) ceramic for use in wear studies was prepared from a commercial tricalcium phosphate. The sintered HAP had physical properties close to those of human enamel. The coefficient of friction and wear of the sintered HAP ceramic as characterized by tangential force, track width, and surface failure data, approximated those of human enamel.
متن کاملSYNTHESIS OF FUNCTIONALLY GRADED Al LM25/ZIRCONIA COMPOSITE AND ITS SLIDING WEAR CHARACTERIZATION USING RESPONSE SURFACE METHODOLOGY
Functionally graded aluminium/zirconia metal matrix composite was fabricated using stir casting technique followed by horizontal centrifugal casting process and a hollow cylindrical functionally graded composite (150 x 150 x 16 mm) was obtained with centrifuging speed of 1200 rpm. The microstructural evaluation and hardness test was carried out on the outer and inner surface of the functionally...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Metal Finishing Society of Japan
سال: 1985
ISSN: 1884-3395,0026-0614
DOI: 10.4139/sfj1950.36.11