Sliding Wear Behavior of AISI 52100 Steel with Pearlitic and Bainitic Microstructures
نویسندگان
چکیده
منابع مشابه
Preparation and Mechanical Properties of Nano/Ultrafine Bainitic Structure in AISI 52100 Steel
The development of nano/ultrafine bainitic structure in AISI 52100 steel was the goal of this study. For this purpose,the AISI 52100 the specimens were austenitized at 1050 °C for 60 min followed by low-temperature austemperingtreatment at different temperatures and times. The austempered samples were characterized using field emissionscanning electron microscopy (FESEM), X-ra...
متن کاملpreparation and mechanical properties of nano/ultrafine bainitic structure in aisi 52100 steel
the development of nano/ultrafine bainitic structure in aisi 52100 steel was the goal of this study. for this purpose,the aisi 52100 the specimens were austenitized at 1050 °c for 60 min followed by low-temperature austemperingtreatment at different temperatures and times. the austempered samples were characterized using field emissionscanning electron microscopy (fesem), x-ray diffraction (xrd...
متن کاملThe Wear Behavior of Textured Steel Sliding against Polymers
Artificially fabricated surface textures can significantly improve the friction and wear resistance of a tribological contact. Recently, this surface texturing technique has been applied to polymer materials to improve their tribological performance. However, the wear behavior of textured tribo-pairs made of steel and polymer materials has been less thoroughly investigated and is not well under...
متن کاملDevelopment of Ultrafine Bainitic Structure in AISI 431 Stainless Steel
The development of ultrafine bainitic structure in AISI 431 stainless steel was the goal of this study. For this purpose, the AISI 431 specimens were austenitized at 1100 °C for 60 min followed by low-temperature austempering treatment at different temperatures and times. Austempered samples were characterized using field emission scanning electron microscopy (FESEM), X-ray diffraction (X...
متن کاملOn the incorporation of length scales associated with pearlitic and bainitic microstructures into a visco-plastic self-consistent model
On the incorporation of length scales associated with pearlitic and bainitic microstructures into a visco-plastic self-consistent model D. Canadinc a,∗,1, H. Sehitoglu a,1, H.J. Maier b,2, P. Kurath a,1 a University of Illinois at Urbana-Champaign, Department of Mechanical Science and Engineering, 1206 W. Green Street, Urbana, IL 61801, United States b University of Paderborn, Lehrstuhl f. Werk...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of Materials Processing
سال: 2011
ISSN: 1225-696X
DOI: 10.5228/kstp.2011.20.7.479