Sıkıştırma Döküm Yöntemi İle Üretilen EN AW 5754 (AlMg3)/SiCp Kompozit Malzemelerde Farklı Takviye Oranlarının Aşınma Davranışları Üzerine Etkisi
نویسندگان
چکیده
In this study, SiCp particles were reinforced at volumetric ratios of 5%, 10%, 15% and 20% into the EN AW 5756 (AlMg3) metal matrix composite by using squeeze casting method. The squeezing process was carried out for 10 seconds under a pressure 80 MPa. changes in wear behaviors friction coefficients 5754/SiCp samples examined under1.0 N force, 5000 cycles with 0.04 m/s sliding speed. As result experiments, it found that coefficient value increased from non-reinforced alloy to 10% SiCp-reinforced composite, while then decreased composites. Moreover, amount material as ratio reinforcement increased, highest occurred composite. This rate deformation statuses materials used experiments conducting SEM (Scanning Electron Microscopy) EDS (Energy-Dispersive Spectrometry) analyses. these examinations, observed 5% reinforcements did not show homogeneous distribution matrix, but homogeneously distributed material.
منابع مشابه
Farkli Etkilesim Yontemlerinin Is Sureci Modelleme Evrelerine Olan Etkisinin Incelenmesi
Öz. Bilgisayar destekli işbirlikçi iş süreci modelleme, coğrafi olarak dağılmış birden fazla kullanıcının birbirleriyle ve kullanılan sistem ile etkileşim kurarak iş süreçlerinin modellenmesine olanak sağlamaktadır. Bu çalışmada farklı etkileşim yöntemi sunan iki sistem üzerinde iki vaka çalışması gerçekleştirilmiştir. Farklı etkileşim yöntemlerinin iş süreci modellemenin ana fazları olan edinm...
متن کاملYazılım Kalite Maliyetleri Üzerine Bir Çalışma - Farklı Sektörlerden Proje İncelemeleri
Graduate and PhD students of METU Informatics Institute have calculated cost of quality of real projects in their own organization as an assignment and analyzed their findings. This study examines the results of these analyses and this type of assignments on industry and on Professional viewpoints of the students who are also participants in the industry. Anahtar kelimeler: Kalite maliyeti, yaz...
متن کاملInfluence of Dentinal Erosion on Shear Bond Strength of Composite Restorations with Different Bonding Systems Dental Erozyonun Farklı Bağlayıcı Ajan Kullanılarak Yapılan Kompozit Restorasyonların Kesme Bağlanma Kuvvetine Etkisi
ÖZET Aim: The aim of the study is to examine the effect of dentinal erosion on shear bond strength of composite restorations. Materials and Methods: A half of 80 dentin pairs were subjected to erosion and toothbrush abrasion (eroded samples) whereas the other half was subjected to toothbrush abrasion (non-eroded samples) during six days. The restorations were bonded with (1) Optibond FL, (2) Ex...
متن کاملAGCF Cozumu icin Gercek-Zamanli Performans Optimizasyonu
Özet. Bu makalede Netas VoIP (Voice over IP) santralinin IMS (IP Multimedya Subsystem)’e erişim verimliliğini artırmaya ve abone kayıt işlemleri sırasında olumsuz etkilenen sistem performansını iyileştirmeye yönelik çalışmalarla ilgili bilgi birikimi ve tecrübe paylaşılmıştır. Bu kapsamda geliştirdiğimiz aramaprogramlama teknikleri ve önerdiğimiz bit haritası yöntemi yardımı ile optimum sayıda ...
متن کاملInfluence of Scanning Strategies on Processing of Aluminum Alloy EN AW 2618 Using Selective Laser Melting
This paper deals with various selective laser melting (SLM) processing strategies for aluminum 2618 powder in order to get material densities and properties close to conventionally-produced, high-strength 2618 alloy. To evaluate the influence of laser scanning strategies on the resulting porosity and mechanical properties a row of experiments was done. Three types of samples were used: single-t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bilecik ?eyh edebali ünivers?tesi fen bilimleri dergisi
سال: 2022
ISSN: ['2458-7575']
DOI: https://doi.org/10.35193/bseufbd.978424