Site Substitution of Additive Elements in TiAl Intermetallic Compound
نویسندگان
چکیده
منابع مشابه
Magnetic phase transitions in intermetallic CeCuGe compound
Electrical and magnetic properties of CeCuGe were investigated through electrical resistivity, thermal conductivity and magnetization measurements in the temperature range 2–300 K. Magnetization measurements indicate a paramagnetic to ferromagnetic transition at TZ10 K, in agreement with previous work. There are two distinct paramagnetic regimes: At high-T the magnetic moment per cerium is 2.50...
متن کاملA XAFS Study on the Site Determination of Additives in the Ni3Al Intermetallic Compound
Occupied sites by dopants of Ag(O.lat%). Pd(Zat%) and Zr(OAat%) in the Ni3AI intermetallic compound are investigated by means of EXAFS analysis. It is found that Pd substitutes the Ni site and Zr substitutes the A1 site. These results are consistent with tthose of channeling enhanced microanalysis. Ag is also determined to substitute in the Ni site by EXAFS and this result supports that Ag addi...
متن کاملMagnetic behaviour of the intermetallic compound YbCo2Si2
We report on a comprehensive study of the magnetic properties of YbCo2Si2 investigated using a single crystal. All data confirm a stable trivalent Yb state carrying a well-localized 4f moment, as well as a non-magnetic Co state. We observed a sizeable anisotropy in the magnetic susceptibility χ(T ), with the moment in the basal plane twice as large as that along the c-direction. Combining this ...
متن کاملControl of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel
The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic comp...
متن کاملMechanical milling of the intermetallic compound AlFe
The intermetallic compound AlFe in its ordered B2 phase has been ground under Ar in a ball-milling device. The system evolution under mechanical work has been examined as a function of time of milling by x-ray diffraction, transmission Mössbauer spectroscopy, and differential scanning calorimetry. Short and long range disorder was observed. The evolution of the long range order parameter with m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1992
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.56.3_232