Sintering of Cu-Al2O3 nano-composite powders produced by a thermochemical route
نویسندگان
چکیده
منابع مشابه
PREPARATION AND SINTERING OF W-20%Wt Cu COMPOSITE POWDERS PRODUCED BY CO-PRECIPITATION METHOD
Abstract: materials can be fabricated by sintering of W-Cu composite powders. In this research W-20%wt Cu composite powderswas synthesized via a co-precipitation method. Precipitate obtained from a mixture of copper nitrate and ammoniumparatungstate (APT) in distilled water contained W-Cu compounds. This precipitate was washed, dried and calcinedat 550 of dried precipitate powder was determined...
متن کاملSintering of a-Al2O3-seeded nanocrystalline g-Al2O3 powders
This paper demonstrates that seeding nanocrystalline transition alumina powders is a viable option for producing high quality, alumina-based ceramics. By using a-Al2O3 concentrations of 51.25 wt.% a-Al2O3 seed particles (equivalent to 5 10 seeds/cm of g-Al2O3) the sintering temperature is reduced from 1600 C for unseeded g-Al2O3 to 1300–1400 C in dry pressed powders. The scale of the sinteredmi...
متن کاملSYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD
The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...
متن کاملNano-size Hydroxyapatite Powders Preparation by Wet-Chemical Precipitation Route
In this study, wet-chemical process was performed to prepare nano-size hydroxyapatite (HA) powders (≈10 nm) by varying concentration (low, medium and high) of the starting solutions in order to increase the amount of as-dried HA powders with different process conditions. Particle sizes and density were analyzed and differential thermal analysis was used to determine the glass transition (Tg) an...
متن کاملSelective Laser Sintering of Nano Al2O3 Infused Polyamide
Nano Al₂O₃ polyamide composites are evaluated for processing by selective laser sintering. A thermal characterization of the polymer composite powders allowed us to establish the possible initial settings. Initial experiments are conducted to identify the most suitable combinations of process parameters. Based on the results of the initial trials, more promising ranges of different process para...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Serbian Chemical Society
سال: 2007
ISSN: 0352-5139,1820-7421
DOI: 10.2298/jsc0711115k