Sintering mechanisms of partially stabilized zirconia (TZ3Y) with ZnO and Co3O4 as sintering additives

Sintering of zirconia pdf

Probing the densification mechanisms during flash sintering of ZnO

Using ZnO as a model system, the densification mechanisms of flash sintering are investigated. Controlled experiments via limiting the maximum current or the effective ramp rate suggest that both the maximum specimen temperature and the high heating rate (on the order of 200 C/s) are essential for the rapid densification during the flash sintering. Moreover, benchmarking rapid thermal annealing...

Sintering properties of zirconia-based ceramic composite

This study examines the effects of different ZrB2 content on various mechanical properties and electrical conductivity of ZrB2/Y-TZP composite. Composites with ZrB2 content of up to 20 wt-% were particularly beneficial at the lower sintering temperature range by achieving greater densification and better hardness than Y-TZP monolith. In contrast to the trends estimated from rule of mixture, the...

The Comparison of MgO and TiO2 Additives Role on Sintering Behavior and Microstructures of Reaction-Sintered Alumina-Zirconia-Mullite Composite

Alumina-Mullite-Zirconia ceramic composites were prepared by reaction sintering of alumina, zircon mixture and the sintering aids of magnesia and titania at temperatures of 1400 and 1600 C for 2 hours. The development of different phases and microstructures of the composites were analysed to assess the relative influence of the additives on the formation of alumina-zirconia-mullite compos...

Effect of impurities on sintering and conductivity of yttria-stabilized zirconia

The effect of low concentrations of Fe203, AI203 and Bi203 on the sintering behaviour of (ZrO2)o.83 (YO1.s)o.17, made by alkoxide synthesis, has been investigated. The best results are achieved with Bi203 as a sinter agent and a relative density of 95% is obtained at 1200 K. The effects of these impurities on the electrical conductivity of the bulk and the grain boundaries has been investigated...