Sintering behaviors and magnetic properties of metal injection molded Fe-Co alloys.

Effect of minor Co additions on the crystallization and magnetic properties of Fe(Co)NbBCu alloys

The effect of partial replacement of Fe by Co (up to 8 %) on thermal stability, structure and magnetic properties of FeNbBCu alloys has been explored in this paper. The results indicate that Co reduces the stability against crystallization of the amorphous alloy and stabilizes the nanocrystalline phase prior to the further precipitation of metastable boride phases. Transmission Mössbauer spectr...

Structure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method

Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer  (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spher...

Magnetic Properties of Platinum Metal Alloys

A number of the papers presented at the International Conference on Magnetism held at the University of Nottingham in September dealt with alloys of the platinum metals. The proceedings will be published shortly by the Institute of Physics and the Physical Society. Papers describing neutron diffraction studies demonstrated the powerfulness of some of the recently developed techniques. Thus G. G...

Effect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets

Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...

Magnetic properties of Al, V, Mn, and Ru impurities in Fe–Co alloys