Sintering and Mullite Formation from Kyanite-Glass System
نویسندگان
چکیده
منابع مشابه
MULLITE SYNTHESIS AND FORMATION FROM KYANITE CONCENTRATES IN DIFFERENT CONDITIONS OF HEAT TREATMENT AND PARTICLE SIZE
The process of mullitization of kyanite concentrate was studied at different conditions of heat treatment (1400– 1600 °C and 0.5 – 3.5 hours) and particle size of raw materials (38-300 ?m). Kyanite concentrate was obtained fromore-dressing of kyanite deposits of Mishidowan-Bafgh region at 100 km northeastern part of Yazd. The results ofmicrostructure (shape, distribution and size of the grains)...
متن کاملMicrowave Sintering of Mullite
Microwave sintering possesses unique attributes and has the potential to be development as a new technique for controlling microstructure and to improve the properties of advanced ceramics. Because microwave radiation penetrates most ceramics, uniform volumetric heating is possible. Thermal gradients, which are produced during conventional sintering because of conductive and radioactive heat tr...
متن کاملSintering behaviour of a glass obtained from MSWI ash
The sintering behaviour of a glass obtained by Municipal Solid Waste Incinerator (MSWI) bottom ash (WG) was investigated and compared with a Na2O–MgO–CaO–SiO2 composition (CG). The sintering activation energy, Esin, and the energy of viscous flow, E , were evaluated by dilatomeric measurements at different heating rates. The formation of crystalline phases was evaluated by Differential Thermal ...
متن کاملModel for sintering polydispersed glass particles
We propose a model to describe the sintering kinetics of polydispersed glass particles, having no adjustable parameter. The model is based on three sintering stages: a pure `Frenkel' (F) ®rst step, a mixed `Frenkel/Mackenzie± Shuttleworth' stage, and a third, pure `Mackenzie±Shuttleworth' (MS) step. The model considers sample shrinkage as the sum of the partial shrinkage of several clusters, ea...
متن کاملStudies on the Formation of Mullite from Diphasic Al2O3-SiO2 Gel by Fourier Transform Infrared Spectroscopy
Al2O3-SiO2 diphasic gel was synthesized by sol gel route from aluminium nitrate and silicic acid following aqueous phase colloidal interaction. The precursor gel powder was thoroughly characterized by chemical analysis, measurement of surface area and bulk density measurement. The gel powder was further characterized by thermogravimetry, XRD diffraction stud...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1993
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.101.1308