SIFAT MEKANIK BETON TANPA AGREGAT KASAR

One of the transitional materials in concrete mixes is Reactive Powder Concrete (RPC). There are several mechanical properties that can be used as a reference when judging quality concrete. The modulus elasticity ratio normal stress to associated strain for tensile or compressive below proportional limit material. modification factor (λ) value reflects reduction lightweight compared weight same strength. Until now, references still only intended In this study tensile, splitting, and tests would carried out on RPC without coarse aggregate which refers American Society Testing Materials (ASTM) standards analyze with Universal Machine (UTM) compressor meter tool aims determine λ sample being tested. After testing cylindrical specimens, specific gravity ranges from 1884,3945 kg/m3 2040,9558 kg/m3, values 20064,2870 MPa 34787,6751 MPa, range 1,1944 1,8665. Abstrak Salah satu bahan transisi dalam campuran beton adalah Adapun beberapa sifat mekanik yang dapat dijadikan acuan untuk menentukan kualitas atau mutu beton. satunya elastisitas, merupakan rasio tegangan terhadap terkait pada tarik tekan di bawah batas proporsionalitas Faktor modifikasi (λ), merefleksikan properti mekanis tereduksi dari ringan, semuanya relatif dengan kuat sama. Acuan ketentuan hingga saat ini hanya ditujukan normal. Oleh karena itu, penelitian dilakukan pengujian tarik, belah, dan elastisitas tanpa agregat kasar jenis menurut standar menganalisa tersebut mesin Mechine alat kompresor bertujuan mengetahui nilai sampel diuji. Setelah benda uji silinder, didapatkan berat berkisar antara sebesar 34787,6751,