Si/Cu-Zn(ox)/C composite as anode material for Li-ion batteries

نویسندگان

چکیده

The silicon based composite Si/Cu-Zn(ox)/C was prepared by ball milling from Si microparticles, Cu-Zn nanopowder heated at air and carbon black. is formed submicrometer particles, Cu-rich CuxZn, CuO, ZnO C nanoparticles. two oxides are electrochemically active during the first discharge, improving nanostructuration of providing Cu nanoparticles that enhance electronic conductivity with CuxZn C. helps to buffer volume variations due Li-Si alloying reactions cycling. further nanostructured cycles as shown XRD electrochemical measurements. material tested anode for Li-ion batteries, a reversible capacity 800 mAh.g−1 100 current 300 mA.g−1 good rate capability. mainly stable after few while solid electrolyte interphase stabilized about ten impedance spectroscopy.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

SnO2 Nanowires on Carbon Nanotube Film as a High Performance Anode Material for Flexible Li-ion Batteries

Today, Li-ion batteries (LIBs) are the most common rechargeable batteries used in electronic devices. SnO2 with theoretical specific capacity of 782 mAh/g is among the best anode materials for LIBs. In this report, Three-dimensional SnO2 nanowires (NWs) on carbon nanotube (CNT) thin film (SnO2 / CNT) is fabricated using a combination of vacuum filtration and thermal evaporation techniques. The ...

متن کامل

Electrochemical properties of iron oxide nanoparticles as an anode for Li-ion batteries

The synthesis of iron oxide nano-particles by direct thermal decomposition was studied. Simultaneous thermal analysis and Fourier transform infrared spectroscopy results confirmed the formation of iron-urea complex, and disclosed iron oxide formation mechanism. Calcination of the iron-urea complex at 200°C and 250°C for 2 hrs. resulted in the formation of maghemite along with hematite as a seco...

متن کامل

Initial Discharge Capacity of Manganese Cobaltite as Anode Material for Lithium Ion Batteries

Nanostructured manganese cobalt oxide spinel (MnCo2O4) are prepared by co-precipitation method and calcined at 650 and 750°C. Morphological studies show that by increasing the calcination temperature from 650 to 750°C, morphology of the particles changes from quasi-plate to polyhedral. The MnCo2O4 calcined at 650°C could deliver an initial discharge capacity of 1438 mAh g-1 under current densit...

متن کامل

Synthesis of Hard Carbon- Silicon Nanocomposite as Anode Active Material for Lithium-Ion Batteries

In this research, using phenolic resin as the precursor of carbon and various amounts of ethylene glycol as a pore former, porous samples of hard carbon were synthesized. Samples were characterized by x-ray diffraction (XRD) and N2 adsorption-desorption methods. Broad diffraction peaks represent the amorphous structure of samples. Moreover, the gas adsorption-desorption curves showed that the a...

متن کامل

Electrochemical properties of cobalt hydroxychloride microspheres as a new anode material for Li-ion batteries

The use of cobalt hydroxychloride [Co2(OH)3Cl] as an anode material for lithium ion batteries (LIBs) is investigated using spherical shape and ultrafine nanocrystals directly formed by spray pyrolysis from spray solution of cobalt chloride salt. Dot-mapping images of the resulting powders reveal a uniform distribution of Co, O, and Cl throughout the powder. The Co2(OH)3Cl powder prepared direct...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Solid State Ionics

سال: 2021

ISSN: ['0167-2738', '1872-7689']

DOI: https://doi.org/10.1016/j.ssi.2021.115774