Shear instability of plastically-deforming metals in high-velocity impact welding
نویسندگان
چکیده
منابع مشابه
Edge cracks in plastically deforming surface grains
A selection of surface crack problems is presented to provide insights into Stage I and early Stage II fatigue crack growth. Edge cracks at 45o and 90o to the surface are considered for cracks growing in single crystals. Both single crystal slip and conventional plasticity are employed as constitutive models. Edge cracks at 45o to the surface are considered that either (i) kink in the direction...
متن کاملMixed-mode Fracture Analyses of Plastically- Deforming Adhesive Joints
A mode-dependent embedded-process-zone (EPZ) model has been developed and used to simulate the mixed-mode fracture of plastically deforming adhesive joints. Mode-I and mode-II fracture parameters obtained from previous work have been combined with a mixed-mode failure criterion to provide quantitative predictions of the deformation and fracture of mixed-mode geometries. These numerical calculat...
متن کاملthe impact of musical texts on the text recall of young learners of english in isfahan junior high schools
abstract although music possesses some kind of power and using it has been welcome by many students in language classrooms, it seems that they take a non-serious image of the lesson while listening to songs and they may think that it is a matter of fun. the main objective of the present study was to investigate whether learning a foreign language through musical texts (songs) can have an impac...
15 صفحه اولPlastically-deforming, Adhesively-bonded Structures: I Experimental Studies
Rate effects for adhesively-bonded joints in steel sheets failing by mode-I fracture and plastic deformation were examined. Three types of test geometries were used to provide a range of crack velocities between 0.1 mm/s and 5000 mm/s: a DCB geometry under displacement control, a wedge geometry under displacement control, and a wedge geometry loaded under impact conditions. Two fracture modes w...
متن کاملCohesive Zone Models and the Plastically-Deforming Peel Test
The peel test is a popular test method for measuring the peeling energy between flexible laminates. However, when plastic deformation occurs in the peel arm(s) the determination of the true adhesive fracture energy, Gc, from the measured peel load is far from straightforward. Two different methods of approaching this problem have been reported in recently published papers, namely: (a) a simple ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Mechanics and Physics of Solids
سال: 2016
ISSN: 0022-5096
DOI: 10.1016/j.jmps.2016.06.002