Specific interactions, structure and properties in segmented polyurethane elastomers
Two sets of segmented polyurethane (PU) elastomers were prepared from 4,4!-methylenebis(phenyl isocyanate) (MDI), 1,4-butanediol (BD) and a polyester or a polyether polyol, respectively. The molecular mass of both polyols was 1000 g/mol. The stoichiometric ratio of isocyanate and hydroxyl groups was 1 and the polyol/total diol ratio changed from 0 to 1 in 0.1 steps. One step bulk polymerization...
متن کاملThe Modification of Polyurethane Foams Using New Boroorganic Polyols (II) Polyurethane Foams from Boron-Modified Hydroxypropyl Urea Derivatives
The work focuses on research related to determination of application possibility of new, ecofriendly boroorganic polyols in rigid polyurethane foams production. Polyols were obtained from hydroxypropyl urea derivatives esterified with boric acid and propylene carbonate. The influence of esterification type on properties of polyols and next on polyurethane foams properties was determined. Nitrog...
متن کاملUrea distribution in renal failure.
An assessment of intracellular urea removed during haemodialysis has been made from urea extraction and plasma urea estimations. An apparent wide variation in the movement of intracellular urea in patients with acute renal failure from obstetric and traumatic causes and with chronic renal failure is reported.A method for the estimation of red cell water urea is presented. In two patients with c...
متن کاملPreparation and bioactive properties of nano bioactive glass and segmented polyurethane composites.
Composites of glutamine-based segmented polyurethanes with 5 to 25 wt.% bioactive glass nanoparticles were prepared, characterized, and their mineralization potential was evaluated in simulated body fluid. Biocompatibility with dental pulp stem cells was assessed by MTS to an extended range of compositions (1 to 25 wt.% of bioactive glass nanoparticles). Physicochemical characterization showed ...
متن کاملEffect of Mechanical Deformation on in Vitro Calcification of Segmented Polyurethane
= Abstract = To investigate why calcification is accelerated by mechanical flexure, in vitro calcification of segmented polyurethane (SPU) under static elongation and dynamic mechanical flexure was performed. After the calcification period, the amount of calcium deposition was increased by elongation, but the amount of calcium deposition per unit area of the elongated surface was relatively sma...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Polymer Journal
سال: 1990
ISSN: 0032-3896,1349-0540
DOI: 10.1295/polymj.22.1065