Separation Mechanism of Cu/Ceramics MA Composite Powders in DC Plasma Spraying
نویسندگان
چکیده
منابع مشابه
Air-plasma spraying colloidal solutions of nanosized ceramic powders
Coatings prepared from nanosized powders were obtained by spraying ethanol-based colloidal solutions into a plasma plume. The powders investigated included 40 nm γ -Al2O3, 75 nm 8 wt% Y2O3-ZrO2, and 750 nm 25 wt% CeO2-ZrO2. Spray distances from approximately 50 to 63 mm were required to achieve significant coating deposition. As observed in the TEM, the typical lamella morphology of air plasma ...
متن کاملPlasma spraying of micro-composite thermal barrier coatings
The thermal barrier coatings (TBCs) by gas tunnel-type plasma spraying exhibited ceramic-composite features consisting of a host oxide matrix ceramic with an embedded second phase material. The densities of the composite TBC were found to be higher than those sprayed with 100wt% ZrO2 or Al2O3. In the coatings produced with powder mixtures of 50wt%, the embedded splats are found to have a relati...
متن کاملPlasma spraying and characterization of chromium carbide – nickel chromium coatings
Chromium carbide – nickel chromium powder Cr3C2-25wt.NiCr was plasma sprayed by a water-stabilized system WSP®. A series of experiments with variable feeding distance was carried out. Basic characterization of coatings was done by XRD, SEM and light microscopy plus image analysis. Microhardness was measured on polished cross sections. The main focus of investigation was on resistances against w...
متن کاملSplat Formation Mechanism in Thermal Spraying*
In order to understand the splat formation process of individual splat deposited by thermal spraying, commercially available Nickel powders with diameter of several tens micrometers were thermally sprayed onto mirror polished AISI304 substrate surface. The deposited splat shows transition phenomenon from splash type to disk one in flattening on collision onto substrate surface according to both...
متن کاملSYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD
The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1993
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.57.9_1078