Self-healing behavior of epoxy-based double-layer nanocomposite coatings modified with Zirconia nanoparticles
نویسندگان
چکیده
This work reports the self-healing behavior of epoxy-based double-layer nanocomposite coatings designed to mitigate corrosion in various industrial applications. Zirconia (ZrO2) nanoparticles were used as a carrier load separately agent, polyethyleneimine (PEI), and inhibitor, imidazole (IM). The loaded ZrO2 with IM PEI doped into epoxy matrix applied on polished steel substrate form pre top layers coatings, respectively. TEM analysis confirms almost globular morphology zirconia particle size 15–25 nm. chemical bonding interactions among species confirmed through FTIR. synergistic effect agent inhibitor demonstrated pH time dependence release agent. A comparative EIS conducted 3.5 wt% NaCl solution reveals that demonstrate improved resistance performance compared blank single layer reinforced coatings. enhanced can be ascribed efficient response external stimuli potentially considered circumvent oil & gas marine
منابع مشابه
Effects of Colloidal Nanosilica on Epoxy-based Nanocomposite Coatings
Epoxy-based nanocomposites were fabricated with different content of colloidal silica nanoparticles such as 10.0, 20.0 and 30.0 wt %, through solution casting. The covalent bonding interfaces, resulting from a ring-opening reaction between silica nanoparticles and epoxy matrix were confirmed by the Fourier transform (FT-IR) infrared spectroscopy. These nanocomposites were characterized for ...
متن کاملHigh-performance starch-modified graphene oxide/epoxy nanocomposite coatings: A glimpse at cure kinetics and fracture behavior
Epoxy is a versatile resin used in different fields such as coatings, colors, colorants, and composites. Adding nano-scale fillers/additives to the epoxy has valued epoxy coatings for engineering applications, and opened the time of advanced epoxy-based nanocomposite coatings. In the present work, graphene oxide GO was chemically functionalized with starch, as a natural polymer, and added to th...
متن کاملCharacterization of Microvascular-Based Self-healing Coatings
A protocol is described to assess self-healing of crack damage in a polymer coating deposited on a substrate containing a microvascular network. The bio-inspired coating/substrate design delivers healing agent to cracks in the coating via a three-dimensional microvascular network embedded in the substrate. Through capillary action, monomer flows from the network channels into the crack plane wh...
متن کاملEpoxy-based Flame Retardant Nanocomposite Coatings: Comparison Between Functions of Expandable Graphite and Halloysite Nanotubes
Whis work presents a study on the flammability of epoxy coatings containing two types of nano-scale fillers as potential flame retardants: expandable graphite (EG) and halloysite nanotubes (HNTs). Both nanocomposites are prepared by incorporation of the same amount of nanofiller into the epoxy resin for the sake of comparison. Fire retardant nanocomposite coatings are cured through a two-stage ...
متن کاملSolid lubricant behavior of MoS2 and WSe2-based nanocomposite coatings
Tribological coatings made of MoS2 and WSe2 phases and their corresponding combinations with tungsten carbide (WC) were prepared by non-reactive magnetron sputtering of individual targets of similar composition. A comparative tribological analysis of these multiphase coatings was done in both ambient air (30-40% relative humidity, RH) and dry nitrogen (RH<7%) environments using the same tribome...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials & Design
سال: 2021
ISSN: ['1873-4197', '0264-1275']
DOI: https://doi.org/10.1016/j.matdes.2021.109839