Selective laser melting processed Ti6Al4V lattices with graded porosities for dental applications
نویسندگان
چکیده
منابع مشابه
Functionally Graded High Strengh Ceramics Obtained by Selective Laser Melting
Henriques B 1,2* 1CMEMS-UMinho, University of Minho, Campus de Azurém, 4800-058 Guimarães, Portugal 2Federal University of Santa Catarina, Campus Blumenau , 89065-300, Blumenau/SC, Brazil *Corresponding author: Henriques B, CMEMS-UMinho, University of Minho, Campus de Azurém, 4800-058 Guimarães, Portugal. Federal University of Santa Catarina, Campus Blumenau , 89065-300, Blumenau/SC, Brazil, E-...
متن کاملCustomized a Ti6Al4V Bone Plate for Complex Pelvic Fracture by Selective Laser Melting
In pelvic fracture operations, bone plate shaping is challenging and the operation time is long. To address this issue, a customized bone plate was designed and produced using selective laser melting (SLM) technology. The key steps of this study included designing the customized bone plate, metal 3D printing, vacuum heat treatment, surface post-processing, operation rehearsal, and clinical appl...
متن کاملNano-second UV laser processed micro-grooves on Ti6Al4V for biomedical applications
Article history: Laser surface texturing can Received 19 October 2007 Received in revised form 29 April 2008 Accepted 5 May 2008 Available online 16 May 2008
متن کاملInfluence of post-processing on Ti6Al4V lattice structures produced by Selective Laser Melting
Selective laser melting (SLM) is a novel technique being increasingly used for the production of porous structures with a high degree of precision and near net shape. These porous materials are finding their use in the biomedical industry for implants. In this thesis, the effect of post-processing using hot isostatic pressing (HIP) and surface modification techniques, such as chemical etching a...
متن کاملPerformance of High Layer Thickness in Selective Laser Melting of Ti6Al4V
To increase building rate and save cost, the selective laser melting (SLM) of Ti6Al4V with a high layer thickness (200 μm) and low cost coarse powders (53 μm-106 μm) at a laser power of 400 W is investigated in this preliminary study. A relatively large laser beam with a diameter of 200 μm is utilized to produce a stable melt pool at high layer thickness, and the appropriate scanning track, whi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Mechanical Behavior of Biomedical Materials
سال: 2019
ISSN: 1751-6161
DOI: 10.1016/j.jmbbm.2018.08.047