Selective catalytic reduction of NO by H2 over Pd/TiO2 catalyst
نویسندگان
چکیده
منابع مشابه
Selective Catalytic Reduction of No Byc3h6 over a Commercial Automotive Iridium Based Catalyst
Ir/TiO2 coated on cordierite monolith was investigated in the selective catalytic reduction (SCR) of NO with propene using a broad temperature range and simulated diesel exhaust gas conditions under the standard mixture (1000 vpm NO, 2000 vpm C3H6, 500 vpm CO, 10 vol.% O2). The physicochemical characterization of the commercial catalyst showed that the BET surface area of the fresh and aged sam...
متن کاملSelective Catalytic Reduction of CuO/SiO2 Nano-composites towards NO Reduction in Gas-phase
The xerogel samples were prepared by hydrolysis and condensation of tetraethyl orthosilicate (TEOS) by the sol-gel method. In this investigation, a new molar ratio of H2O/TEOS was determined to be 11.7. Also, the necessary amounts of tri-hydrated copper nitrate and penta-hydrated copper sulfate were added to the solution in such a manner that the concentration of the copper oxide in final solut...
متن کاملNOx Selective Catalytic Reduction over Pt Supported Catalyst Promoted by Zeolite and CeO2-ZrO2
The emission control of NOx in exhaust gases is one of the greatest engineering challenges to extend the practical and commercial application of diesel and lean burn engines. One solution is selective NOx reduction using hydrocarbons in an oxidizing atmosphere. We mainly focused on catalytic reactions under temperature excursion because of the resemblance to conditions prevailing in real automo...
متن کاملIron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3.
The catalysts of iron-doped Mn-Ce/TiO2 (Fe-Mn-Ce/TiO2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction (SCR) of NO with NH3. It was found that the NO conversion over Fe-Mn-Ce/TiO2 was obviously improved after iron doping compared with that over Mn-Ce/TiO2. Fe-Mn-Ce/TiO2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity. The results...
متن کاملLow temperature selective catalytic reduction of NOx with NH3 over Mn-based catalyst: A review
The removals of NOx by catalytic technology at low temperatures (100–300 °C) for industrial flue gas treatment have received increasing attention. However, the development of low temperature catalysts for selective catalytic reduction (SCR) of NOx with ammonia is still a challenge especially in the presence of SO2. The current status of using Mn-based catalysts for low temperature SCR of NOx wi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chinese Journal of Catalysis
سال: 2019
ISSN: 1872-2067
DOI: 10.1016/s1872-2067(19)63297-3