Secular change in corrosion rate of cold rolled 5083 aluminum alloy in alkaline solution.
نویسندگان
چکیده
منابع مشابه
CORROSION BEHAVIOR OF 6063 ALUMINUM ALLOY IN ETHYLENE GLYCOL-WATER SOLUTION
The electrochemical behavior of 6063 aluminum alloy in ethylene glycol-water mixture was investigated by polarization curves and AC impedance measurements (EIS). The results obtained from polarization curves showed that corrosion rate decreased with increasing ethylene glycol concentration. EIS data showed the decrease in the interface capacitance which caused by adsorption of ethylene glycol ...
متن کاملMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملFatigue and Anisotropic behaviours of cold rolled AA1200 Aluminium Alloy
This study examines the fatigue and anisotropy behaviour of cold rolled AA1200 aluminium alloy for light weight automotive connecting rod application. Aluminium (Al) 1200 ingots were melted at temperature of 680 0C (after one hour of heating) cast in sand mould and cast samples homogenized for 6 hrs at 480 0C. The cold rolling process was carried out after homogenisation for 10, 20, 30, 40 and ...
متن کاملEffect of welding parameters on penetration depth in FB-TIG welding of 5083 aluminum alloy
In the present study, effect of current, welding speed and preheat temperature during FB-TIG welding of AA5083 aluminum alloy was studied. Using the Taguchi method, 9 different tests were designed to investigate the effect of welding parameters on the penetration depth. Consistent with predictions, increasing the current and preheat temperature, and reducing the welding speed led to an increase...
متن کاملEffect of welding parameters on penetration depth in FB-TIG welding of 5083 aluminum alloy
In the present study, effect of current, welding speed and preheat temperature during FB-TIG welding of AA5083 aluminum alloy was studied. Using the Taguchi method, 9 different tests were designed to investigate the effect of welding parameters on the penetration depth. Consistent with predictions, increasing the current and preheat temperature, and reducing the welding speed led to an increase...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1995
ISSN: 0451-5994
DOI: 10.2464/jilm.45.273